Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Preparation and property of a novel Al3+-doped silica gel adsorptive material

PREPARATION AND PROPERTIES OF Al3+ DOPED SILICA GEL ADSORBENT WITH CERAMIC FIBER MATRIX

Adsorptive Performance of Metallic Ion Doped Silica Gel Adsorbent

Silica gel adsorbents doped with Al, Ti, and Co ions improved adsorption capacity, thermal stability and aging resistance

Study on Monolithic Ti-Doped Silica Gel Adsorbent Based on Ceramic Fiber

CHARACTERIZATION AND PERFORMANCE OF METALLIC DOPED SILICA GEL ADSORBENT

MONOLITHIC ADSORBENT OF TITANIUM-DOPED SILICA GEL

Synthesis of porous silica gel and study on the adsorption of cerium

Aluminium modified silica-gel adsorbent material and its preparing process

Study On The Ti-Doped Silica Gel Adsorptive Functional Paper

Dendrimer-based Preparation of Mesoporous Alumina Nanofibers by Electrospinning and Their Application in Dye Adsorption

Preparation of Zinc-Doped Silica Gel Materials and Their Adsorptive Performance

PREPARATION AND PROPERTIES OF SILICA GEL FUNCTIONAL SHEET

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Preparation and adsorptive performance of silica gel/molecular sieve composites

Synthesis and Adsorption Behavior of Magnesium Silicate Gels

Preparation and Crystallization of Si-Al Gel

Influence of synthesis variables of a sol-gel process on the properties of mesoporous alumina and their fluoride adsorption

Preparation and Characterization of a Novel Silica Aerogel As Adsorbent for Toxic Organic Compounds

Creating the Adsorptive Sites with High Performance Toward Nitrosamines in Mesoporous Silica MCM-41 by Alumina Modifier

Preparation of Organically Functionalized Silica Gel As Adsorbent for Copper Ion Adsorption