Abstract:We report the synthesis, characterization, and electrochemistry properties of ribbon- and boardlike nanostructures of nickel hydroxide, which crystallize in different phases. The ribbonlike nanostructures (nanoribbons) of nickel hydroxide were synthesized by treating amorphous alpha-Ni(OH)2 with high concentrations of nickel sulfate. These nanoribbons crystallized in a new phase had typical widths of 5-25 nm, thicknesses of 3-9 nm, and lengths of up to a few micrometers. After further treatment in alkali at 60 degrees C, the nanoribbons converted to boardlike nanostructures (nanoboards), which crystallized in the beta-phase with the average length-width-thickness ratio of 20:6:1. The crystal structures, Raman spectra, and electrochemical properties of these nanostructures of nickel hydroxide are described in this paper. For comparison, the amorphous alpha-Ni(OH)2 has also been investigated. Moreover, the intermediate product between the nanoribbons and the nanoboards displays a unique structure, which implied an interesting transformation process. The nanoribbons with the new phase show some unique features in Raman spectra, two new peaks located at 3534 and 3592 cm(-1) in the OH stretching region, indicating the new chemical environment of the hydroxyl groups. The nanoboards exhibit the highest specific capacity, which is close to the theoretical capacity of beta-Ni(OH)2. It suggests that the boardlike nanostructure is helpful in improving the electrochemical performance of nickel hydroxide. Because of their unique structures and properties, the nanoribbons and nanoboards of nickel hydroxide may give a new perspective for applications in the areas of catalysts and rechargeable batteries.

Synthesis of nickel hydroxide nanoribbons with a new phase: A solution chemistry approach

Solution-phase synthesis of nickel phosphide single-crystalline nanowires

Ribbon- and Boardlike Nanostructures of Nickel Hydroxide: Synthesis, Characterization, and Electrochemical Properties

Solution Phase Synthesis Of Magnesium Hydroxide Sulfate Hydrate Nanoribbons

Rationally synthetic strategy: from nickel hydroxide nanosheets to nickel oxide nanorolls

Synthesis and electrochemical evaluation of nickel hydroxide nanosheets with phase transition to nickel oxide

Solution-Phase Synthesis of Single-Crystal CuO Nanoribbons and Nanorings

Synthesis and Characterization of Ni(OH)2 Single-crystal Nanorods

Preparation of Anisotropic Transition Metal Phosphide Nanocrystals: the Case of Nickel Phosphide Nanoplatelets, Nanorods, and Nanowires

Phase-controlled Synthesis of Nickel Silicide Nanostructures

Direct Syntheses of Mixed Ion and Electronic Conductors La<sub>4</sub>Ni<sub>3</sub>O<sub>10</sub>and La<sub>3</sub>Ni<sub>2</sub>O<sub>7</sub>from Nanosized Coprecipitates

Hydrothermal Synthesis of Needle-Like Hyperbranched Ni(So4)(0.3)(Oh)(1.4) Bundles and Their Morphology-Retentive Decompositions to Nio for Lithium Storage

Electrolytic approach towards the controllable synthesis of NiO nanocrystalline and self-assembly mechanism of Ni(OH)2 precursor under electric, temperature and magnetic fields

Controlled Fabrication and Property Studies of Nickel Hydroxide and Nickel Oxidenanostructures

Inducing Abundant Magnetic Phases and Enhancing Magnetic Stability by Edge Modifications and Physical Regulations for NiI2 Nanoribbons

Solution Phase Synthesis of Cu(Oh)(2) Nanoribbons by Coordination Self-Assembly Using Cu2s Nanowires As Precursors

Facile Synthesis of Ni3(BO3)2 Nanoribbons and Their Antimicrobial, Electrochemical and Electrical Properties

Synthesis and growth mechanism of sponge-like nickel using a hydrothermal method

Controlled Synthesis of Single-Crystalline Li0.44mno2 and Li2mno3 Nanoribbons

Synthesis of Single-Crystal Niobium Pentoxide Nanobelts

Morphology and Electrochemical Performance of Nano-Scale Nickel Hydroxide Prepared by Supersonic Coordination-Precipitation Method