Abstract:Acetic acid lignin (AAL) obtained from Bagasse was used as a partial substitute of polyols for polyurethane (PU) adhesive due to the presence of reactive sites, i.e. aliphatic and aromatic hydroxyl groups, in its structure. To improve its reactivity, lignin is partly demethylated before the copolymerization with polyisocyanate. The demethylation, catalyzed by hydrobromic acid solution under heating conditions, resulted in a decrease of methoxy groups on the phenyl ring and the increase of phenolic hydroxyl groups. It is found that 120 ℃ is the preferred temperature for the demethylation resulted in a 36.5 % increase in hydroxyl content of lignin up to 5.25 mmol/g. Lignin-based polyurethane adhesives were prepared in two steps including preparing a prepolymer based on mixtures of toluene-2,4-diisocyanate (TDI) and unmodified or demethylated lignin, and then the polymerization was completed by adding polyethylene glycol (PEG). The mass ratio (1:1) of TDI: (lignin + PEG) in the compositions was here investigated. The results indicated that the presence of lignin (with and without demethylation) in polyurethane adhesives increased the glass transition temperature, Young’s modulus, and elongation at break. Particularly, the tensile strength was increased by 15–36 MPa with the addition of 10–30 wt% of lignin. Lignin with higher amount of hydroxyl groups prepared by partly demethylation is better integrated into the three-dimensional cross-linking networks of the covalent polymer as a substitute of polyols. Compared to those PU adhesives based on the raw AAL, the adhesives prepared by demethylated lignin have higher tensile strength and thermal stability. It indicates that the demethylation is effective and it is a good strategy to prepare lignin-based PU adhesive with favorable mechanical properties.

Modification of Oxygen Alkaline Wheat Straw Lignin and Its Application in Polyurethane Synthesis

Synthesis of Polyurethane by Use of Wheat Straw Oxygen-Alkaline Lignin and its Properties

Characteristics of oxygen-alkali lignin and its application in synthesis of polyurethane

Study On Effects Of Isocyanate Index And Plasticizer On Lignin-Based Polyurethane

Modification of Renewable Resources-Lignin-by Three Chemical Methods and Its Applications to Polyurethane Foams

Research Development of Lignin Chemical Modification and Its Application on the Synthesis of Polyurethane

Preparations and Properties of Polyurethane Adhesives Modified by Corn Straw Lignin

High-value utilization of hydroxymethylated lignin in polyurethane adhesives.

Modification of Ozone-Oxidized Straw Alkaline Lignin

Optimization of Synthetic Conditions for Lignin-based Polyurethane Film

Preparation of a Polyhydric Aminated Lignin and Its Use in the Preparation of Polyurethane Film

Preparation and Performance of Lignin-Based Waterborne Polyurethane Emulsion

Signally improvement of polyurethane adhesive with hydroxy-enriched lignin from bagasse

Ozone Oxidized Lignin-Based Polyurethane with Improved Properties

Application of Organosolv Lignin in Lignin Modified Polyurethane

Aging Characterization of Straw Alkali-lignin Modified Polyurethane Film

Study on EH Lignin as a Novel Additive for Polyurethane Industry

In Situ Synthesis of Flowerlike Lignin/ZnO Composite with Excellent UV-Absorption Properties and Its Application in Polyurethane

EFFECT OF MODIFICATION BY PHENOLATION ON STRUCTURES OF WHEAT STRAW SODA LIGNIN AND PROPERTIES OF LIGNIN-BASED PHENOL FORMALDEHYDE ADHESIVE

Highly Resilient Lignin-Containing Polyurethane Foam

Synthesis Of Polyurethane Composite With Lignocellulosic Material