Abstract:Purpose - This paper sets out to study the corrosion of No. 20 carbon steel without film and with films of different qualities in high-temperature boiler water with different Cl- concentrations. Design/methodology/approach - The static simulated experiment in high-pressure autoclave and the surface analysis methods of EPMA and XRD were carried out to study the corrosion effect. Findings - Under the following conditions: T = 360 +/- 3 degrees C, pH = 9.40 +/- 0.10, c(o2) < 0.020 mg/l, the density of pitting corrosion on specimens without a protective film increased with the increase of C-Cl(-) content, while C-Cl(-) was > 0.2 mg/l. The film on specimens with integral films would not dissolve observably even until the C-Cl(-) concentration was as high as 0.8 mg/l. Films with corrosion pits would begin dissolving when the Cl- concentration reached 0.4 mg/l. The main constituents of the oxidative films in the gas and liquid phases both were Fe3O4. Practical implications - In order to prevent carbon steel from corroding in boiler water containing Cl- under conditions of low-phosphate and low-sodium hydroxide treatment, the concentration of Cl- should be strictly controlled. Originality/value - it was found that the presence of excessive Cl- in boiler water accelerated the corrosion of No. 20 carbon steel and the maximum permissible concentration of Cl- under the conditions (temperature and pressure) of sub-critical drum boilers was 0.2 mg/l. The research results can provide theoretical guidelines for preventing the facilities of power plants from corroding.

Study on effects of modified lignosulfonate GCL2 on corrosion inhibition performances of carbon steel

Study of Corrosion and Scale Inhibition Performances of Modified Lignosulphonate GCL2-D1

Preparation of Modified Lignosulfonate Corrosion Inhibitor

Study on the Preparation and the Properties of Green Corrosion and Scale Inhibitor GCL2

Effectiveness of an amine-based inhibitor—guanidine for steel in chloride-contaminated concrete

Study on Synergistic Corrosion Inhibition Effect between Calcium Lignosulfonate (CLS) and Inorganic Inhibitors on Q235 Carbon Steel in Alkaline Environment with Cl−

The Influence of Chlorides on Corrosion Behavior of Carbon Steel in Slag Based Geopolymer Pore Solution

Evaluation of Ginkgo leaf extract as an eco-friendly corrosion inhibitor of X70 steel in HCl solution

STUDY ON CORROSION INHIBITION PERFORMANCE OF NON-WOODY MAGNESIUM LIGNOSULFONATE AND ITS OXIDATION REACTION

Corrosion and Scale Inhibition Properties of Sodium Lignosulfonate and Its Potential Application in Recirculating Cooling Water System

A study of the influence of chloride ion concentration on the corrosion behavior of carbon steel in phosphate high-temperature boiler water chemistries

Corrosion Inhibition of Polyethylene Glycols of Different Molecular Weight on Carbon Steel

Study of the Inhibitors of the Carbon Steel in Dynamic Hot Seawater

Carbon steel anticorrosion performance and mechanism of sodium lignosulfonate

Effect of Chloride Ion Concentration in Sodium Chloride Solution Saturated with Carbon Dioxide on Corrosion Behavior of 2Cr13 Stainless Steel

Lignin Terpolymer for Corrosion Inhibition of Mild Steel in 10% Hydrochloric Acid Medium

Investigation of the Corrosion Characteristics and Corrosion Inhibitor Action on J55 Steel in Produced Water

CO2 Corrosion of Low Carbon Steel Under the Joint Effects of Time-Temperature-Salt Concentration

A Glycine Derivative As Corrosion Inhibitor for Carbon Steel in 3.5 Wt% NaCl Solution: the Combined Experimental and Theoretical Calculation

Corrosion inhibition performance of benzimidazole derivatives for protection of carbon steel in hydrochloric acid solution

Effects of Cl- and SO4 2- ions on corrosion behavior of X70 steel