Abstract:Magnetite (Fe3O4) nanoparticles in the interval of 9 similar to 12nm have been synthesized by an non-alkoxide sol-gel method. Through this simple technique, sol-gel materials were prepared from ethanolic solutions of metal chlorides without the need for alkoxides, polymeric gel agents, or elaborate reaction schemes. The gel formation has been studied, and the research shows that gel formation appears to be driven primarily by the formation of an Fe(III)-based network which incorporates Fe(II) into its nanoscale solid domains. The research of the annealing process indicates that magnetite (Fe3O4) nanoparticles can be obtained by annealing only under vacuum, but not in air. Future, Fe3O4 can be oxidized to Fe2O3, as evidenced by XRD, and VSM. The phase structures, morphologies, and particle sizes of Fe3O4 nanoparticles were characterized by thermogravimetric-differential thermal analysis (TG-DTA), X-ray Diffraction (XRD) and Transmission Electron Microscopy (TEM). The results indicate that magnetite (Fe3O4) nanoparticles are homogeneous and have near-spherical shape with a narrow distribution in particle size. Finally, an investigation of the possible mechanism of Fe3O4 nanoparticles formation was performed. Both TG-DTA and X-ray Diffraction (XRD) studies suggest that the reaction of the decomposition of the precursor under vacuum conditions leads to Fe3O4 nanoparticles, while the precursors in air atmosphere is directly oxidized to gamma iron oxide. In addition, this approach may suggest a general route to produce complex multicomponent metal oxide in which the nanoscale oxide is stabilized and spatially distributed.

Synthesis of Nanocrystalline Magnetite (Fe3O4) Films by Self-Reduction Sol-Gel Route

Synthesis of Nanocrystalline Magnetite (Fe<sub>3</sub>O<sub>4</sub>) Films by Self-Reduction Sol-Gel Route

Nanostructured Magnetite (fe3o4) Thin Films Prepared by Sol–gel Method

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

A Non-Alkoxide Sol-Gel Method for the Preparation of Magnetite (fe3o4) Nanoparticles

Aqueous Solution Preparation, Structure, and Magnetic Properties of Nano-Granular Zn x Fe 3− x O 4 Ferrite Films

Aqueous Solution Preparation, Structure, and Magnetic Properties of Nano-Granular Zn<sub><it>x</it></sub>Fe<sub>3−<it>x</it></sub>O<sub>4</sub> Ferrite Films

Preparation and Magnetic Properties of Magnetite Nanoparticles by Sol–gel Method

Microemulsion Synthesis and Characterization of Nano-Fe3O4Particles and Fe3O4Nanocrystalline

Synthesis of Monodisperse Magnetite Nanocrystals Via Partially Reduced Precipitation Method

Preparation of Water-Soluble Magnetite Nanocrystals Through Hydrothermal Approach

Synthesis of Magnetite Nanorods Through Reduction of Β-Feooh

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Single-crystalline Fe3O4 Nanosheets: Facile Sonochemical Synthesis, Evaluation and Magnetic Properties

Synthesis of Superparamagetic Iron Oxide Nanoparticles in Carbon Reduction Method

Synthesis and electrochromic characterization of nanocrystalline NiO thin films prepared by sol-gel method

Large Low-Field Magnetoresistance in Nanocrystalline Magnetite Prepared by Sol-Gel Method

Large Low Field Magnetoresistance In Ultrathin Nanocrystalline Magnetite Fe3o4 Films At Room Temperature

Surface Morphology and Magnetic Properties of CoFe2O4 Thin Films Prepared via Sol–Gel Method

A Facile Synthetic Pathway of Monodisperse Fe3O4 Nanocrystals

Structure and magnetic properties of CoFe2O4 nanocrystal thin films prepared by sol-gel method