Abstract:Porous carbon materials have been studied as anodes in Li-ion batteries for several decades. Interestingly, there is a phenomenon that is still not explicit, in which the specific capacity gradually increases during cycling, especially at a large current rate. Herein, this work demonstrates that the mechanism of increasing capacity is related to the doped transition metal in carbon materials and conducted current rate for the first time. Specifically, the transition-metal-free carbon shows a general electrochemical cycling performance of a gradually fading capacity at a large current rate. However, the capacity of transition-metal-doped carbon is dramatically increased after an initial slow decrease. Also, for the transition-metal-doped materials cycled at a low current rate, a loose and thick solid electrolyte interphase grows, resulting in severe decomposition of electrolyte, sluggish Li-ion diffusion, and a fading capacity during extensive cycling. With a large current rate, the solid electrolyte interphase is more compact, flat, and thin, which significantly decreases the diffusion length of Li ions and alleviates the decomposition of electrolyte on electrode surfaces. Moreover, the components and morphologies of solid electrolyte interphases after cycling at both small and large current rates are investigated through atomic force microscopy and X-ray photoelectron spectroscopy. The mechanisms behind the increased capacity are revealed. These results present a comprehensive understanding of the increased-capacity phenomenon and guidelines for designing high-performing carbon materials.

Influence of phosphorus-doping on lithium intercalation behavior of hard and soft carbons

Preparation of Phosphorus-Doped Carbon and its Performance of Lithium Intercalation

The Effect of Boron Doping on Lithium Intercalation Performance of Boron-Doped Carbon Materials

Lithium Intercalation Performance of P-Doped Phenolic Resin Pyrolysis Carbon

Preparation of Boron-Doped Hard Carbon and Investigation on Its Performance of Lithium-Intercalation

Unveiling the Structure-Activity Relationship of Hollow Spindle-Like Α-Fe2o3 Nanoparticles Via Phosphorus Doping Engineering for Enhanced Lithium Storage

Phosphorus-doped Carbon As Cathode Material for High Energy Nonaqueous Li-O2 Batteries

Preparation and structure study of phosphorus-doped porous graphdiyne and its efficient lithium storage application

P-Doping a Porous Carbon Host Promotes the Lithium Storage Performance of Red Phosphorus

Phosphate-Induced Reaction to Prepare Coal-Based P-Doped Hard Carbon with a Hierarchical Porous Structure for Improved Sodium-Ion Storage

Structural Aspects of Lithiated Carbon

Phytic acid assisted formation of P-doped hard carbon anode with enhanced capacity and rate capability for lithium ion capacitors

In Situ Revealing the Electroactivity of P ? O and P ? C Bonds in Hard Carbon for High‐Capacity and Long‐Life Li/K‐Ion Batteries

P-doped hard carbon material for anode of sodium ion battery was prepared by using polyphosphoric acid modified petroleum asphalt as precursor

Rationally regulating P-doping species to realize ultrastable potassium storage of carbon anode

Investigating the increased-capacity mechanism of porous carbon materials in lithium-ion batteries

Nitrogen and phosphorus co-doped carbon for improving capacity and rate performances of potassium ion batteries

B‐Doped Carbon Coating Improves the Electrochemical Performance of Electrode Materials for Li‐Ion Batteries

Phosphorus-doped porous carbon derived from rice husk as anode for lithium ion batteries

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Phosphorus-doped lithium- and manganese-rich layered oxide cathode material for fast charging lithium-ion batteries