The Preparation and Electrochemical Performance of α-Ni(OH)2 with Different Al Contents
Qian Zhang,Yanhui Xu,Xiaolin Wang
DOI: https://doi.org/10.3321/j.issn:1002-185X.2006.05.005
2006-01-01
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
Abstract:In this paper, α-Ni(OH)2 with different Al contents was prepared by a homogeneous precipitation method. The microstructure was characterized by FT-IR and XRD, and the composition of the samples was analyzed with inductive coupled plasma (ICP). Galvanostatic charge-discharge, cyclic voltammetry and impedance spectroscopy were used to measure the electrochemical behavior of samples. Results show that the stable α-Ni(OH)2 phase can be obtained for the samples with Al contents in the range of 5wt%~20wt% by the homogeneous precipitation method. And the alkali salt with the same structure as α-Ni(OH)2 is obtained without Al addition. According to ICP, there is big difference between the Al contents in the practical solution and the addition, and this difference increases with the decrease of Al addition contents. The specific capacity of discharge increases first, then decreases with the Al contents decreasing, and the charge potential decreases first, then increases. The discharge potential changes little first, then decreases promptly. For the samples with Al contents in the range of 5wt%~20wt%, the diffraction peaks move towards high diffraction angle after cycled for 50 times. However, the α-Ni(OH)2 structure still remains. The sample without Al addition transforms into α-Ni(OH)2 after cycling 50 times and the structure is destroyed heavily.