The electrochemical behavior of Ni(OH)2 in KOH solution containing aluminum hydroxide

Qian Zhang,Yanhui Xu,Xiaolin Wang

DOI: https://doi.org/10.1016/j.matchemphys.2004.03.029

IF: 4.778

2004-01-01

Materials Chemistry and Physics

Abstract:In this paper Co-doped Al-substituted α-Ni(OH)2 was prepared by a homogeneous precipitation method and its electrochemical behavior, in two kinds of electrolyte (7M KOH solution and 7M KOH saturated with Al(OH)3), was investigated by galvanostatic charge-discharge method, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The electrochemical properties of the commercial β-Ni(OH)2 in both electrolyte was also studied in order to compare with that of α-Ni(OH)2. The results show that Co-doped Al-substituted α-Ni(OH)2 has the largest capacity in 7M KOH solution (300mAhg−1). The addition of Al to KOH solution is harmful to the reversible capacity and cycle life of both α-Ni(OH)2 and β-Ni(OH)2. X-ray diffraction (XRD) patterns show that, for Co-doped Al-substituted α-Ni(OH)2, its turbostratic structure maintains after cycles in both alkaline electrolyte, despite the interlayer distance becoming smaller. For β-Ni(OH)2, however, γ-NiOOH species appeared after cycling in both electrolyte and its content is higher after cycling in 7M KOH saturated with Al(OH)3. And adding Al into KOH solution caused the decrease of solution conductivity and increased the apparent diffusion coefficient which is evidenced by electrochemical impedance spectroscopy.