Branched fluorine/adamantane interfacial compatibilizer for synchronously enhancing interlaminar shear strength and wave‐transparent performances of PBO fibers/cyanate ester laminated composites
Zheng Liu,Xiaoli Fan,Muyi Han,Hao Li,Junliang Zhang,Lixin Chen,Qiju Zhu,Junwei Gu
DOI: https://doi.org/10.1002/cjoc.202200749
IF: 5.56
2023-01-05
Chinese Journal of Chemistry
Abstract:Comprehensive Summary Branched fluorine/adamantane PBO precursor (preFABPBO), synthesized via random co‐condensation between 2,2‐bis(3‐amino‐4‐hydroxyphenyl)hexafluoro propane, 1,3‐adamantanedicarbonyl dichloride, and trimesoyl chloride, is performed as interfacial compatibilizer, bisphenol A dicyanate ester (BADCy) resin as polymer matrix, and poly(p‐phenylene‐2,6‐benzobisoxazole) (PBO) fibers as reinforcements to prepare PBO fibers/FABPBO‐BADCy wave‐transparent laminated composites by high temperature molding. The mechanical properties, wave‐transparent performances, and heat resistances of PBO fibers/BADCy composites are simultaneously improved by the addition of preFABPBO. The interlaminar shear strength (ILSS) and flexural strength of PBO fibers/FABPBO‐BADCy composites are 48.9 and 665.3 MPa, respectively, increased by 33.2% and 13.3% compared to those of PBO fibers/BADCy composites (36.7 and 587.4 MPa). The dielectric constant and dielectric loss values at 106 Hz are 2.53 and 0.003, respectively, lower than those of PBO fibers/BADCy composites (3.06 and 0.006), and the corresponding wave transmission efficiency is 94.8%, which also presents excellent stability over the wide temperature (25~200oC) and frequency range (103~107 Hz and 8.2~12.4 GHz). Meanwhile, the heat resistance index and glass transition temperature are 229.9oC and 247.5oC, also better than those of PBO fibers/BADCy composites (229.6oC and 247.1oC). This article is protected by copyright. All rights reserved.
chemistry, multidisciplinary