Flow stress and softening behavior of wrought magnesium alloy AZ31B at elevated temperature

Lingyun Wang,Yongge Fan,Guangjie Huang,Guangsheng Huang
IF: 3.752
2003-01-01
Transactions of Nonferrous Metals Society of China
Abstract:The flow stress and softening behavior of AZ31B magnesium alloy in hot compression were investigated. The relationship of flow stress, temperature and strain rate was appropriately described with the exponential form of Zener-Hollemen parameter during steady state deformation of alloy at 573-723 K, 0.01-5s(-1). Dynamic recrystallization is the softening mechanism of AZ31B in hot compression. The flow curves of alloy have almost no peak value at 723 K and lower strain rate, presenting feature of geometric dynamic recrystallization.