Abstract:Effective removal of toxic metal Ni(II) from wastewater is essential to water safety and human health. Although zeolitic imidazolate framework-8 (ZIF-8) has demonstrated outstanding selective removal of Ni(II) in highsalinity wastewater, the practical applications of ZIF-8 are mainly limited by low active sites utilization, slow adsorption kinetics and poor reusability. In this study, we prepared a novel negatively charged poly (sodium 4-styrenesulfonate) (PSS)-modified ZIF-8 adsorbent, ZIF-8@PSS (12 h), which increased the adsorption rate of Ni (II) (kinetic constant k = 0.0299 g mg(-1) min(-1)) by nearly 10 times and the adsorption capacity (329.58 mg/g) by 1.6 times compared to pristine ZIF-8 (k = 0.0021 g mg(-1) min(-1)). ZIF-8@PSS (12 h) (0.5 g/L) could quickly decrease Ni(II) (C0 = 1.0 mg/L) to 0.1 mg/L (discharged standard) in 25 min, while 600 min for ZIF-8. Batch experiments and characterization analyses revealed PSS can improve particle dispersion, increase active sites utilization, and strengthen Ni(II) diffusion kinetics, thereby enhancing the adsorption of Ni(II). Among them, the increase in active sites utilization of ZIF-8 contributes 83.3% to capacity improvement, while the -SO3- on PSS is 16.7%. Furthermore, the enhancements of adsorption kinetics and capacity were also applicable to other heavy metals (e.g., Cu2+, Pb2+, Cr3+, Cd2+). Column experiments using real nickel plating effluent shown that 1 g ZIF-8@PSS (12 h) could produce similar to 3675 mL of clean water before breakthrough (Ni2+ < 0.1 mg/L). Moreover, a specific nickel chelator, dimethylglyoxime was used to regenerate the exhausted adsorbent and showed an insignificant capacity loss after four cycles. This study indicates the potential of ZIF-8@PSS (12 h) to remove Ni (II) from nickel plating effluent.

Treatment of Nickel-contented Wastewater by Adsorption with Mg(OH)2

The Treatment of Chromium-Contented Wastewater Using Mg(OH)2

A Comparative Study Of Nickel(Ii) Removal From Electroplating Wastewater By Pre-Precipitation Combined With Fenton-Precipitation Or Fenton-Like-Precipitation

Characteristics and Mechanisms of Ni(II) Removal from Aqueous Solution by Chinese Loess

Application of a Novel Strategy—advanced Fenton-chemical Precipitation to the Treatment of Strong Stability Chelated Heavy Metal Containing Wastewater

Study on adsorption of magnesium hydroxide

Treatment of Electroplating Wastewater Containing Nickel by Fenton Oxidation-Ferrite Process

Sorption enhancement of nickel(II) from wastewater by ZIF-8 modified with poly (sodium 4-styrenesulfonate): Mechanism and kinetic study

Preparation and application of MgO-loaded tobermorite to simultaneously remove nitrogen and phosphorus from wastewater

Ion Imprinted Adsorbent for the Removal of Ni(II) from Waste Water: Preparation, Characterization, and Adsorption

Mn3O4–MnOOH nanocomposites for the adsorption-based removal of nickel ions from wastewater

Treatment of Wastewater Containing Nickel with Bulk Liquid Membrane

Nickel ion removal by porous potassium magnesium titanate made from plate-like crystals

Enhanced Removal of Nickel(ii) from Water by Utilizing Gel-Type Nanocomposite Containing Sub-5 Nm Hydrated Manganese(iv) Oxides

Adsorption performance and mechanism of MgO-loaded tobermorite for Mn 2+ with high concentration in wastewater

Graphene/δ-MnO2 Composite As Adsorbent for the Removal of Nickel Ions from Wastewater

Preparation of nano-meter x-zeolite and its application in nickel ion2+ treatment

Recyclable magnetic nickel ferrite–carboxymethyl cellulose–sodium alginate bio-composite for efficient removal of nickel ion from water

Highly Efficient Co-Removal of Heavy Metals in Wastewater from Chemical Oxygen Demand Testing Instrument by Cysteine-Functionalized Magnetic Nanoparticles

Efficient removal of Cr(VI) using recycled MgO from laterite nickel ore by fly ash doping

Highly effective removal of nickel ions from wastewater by calcium-iron layered double hydroxide