Conversion of waste heat to electricity using a high performance pyroelectric converter

Michio Ikura,Jianlin Yu

2003-01-01

Abstract:The pyroelectric coefficients of a 60/40 P(VDF-TrFE) film under high voltage were measured as a function of temperature. When heating at 28 MV/m (700V/25mum), they increased almost linearly from 110 muC/m2K at 35oC to 730 muC/m2K at 60oC but they decreased to as low as 480 muC/m2K between 60oC and 80oC. However, they increased rapidly again above 80oC and reached as high as 1035 muC/m2K at 92oC where 60/40 P(VDF-TrFE) underwent phase transition. Similar measurements at 20 MV/m (500V/25mum) showed the phase transition near 70oC. However, pyroelectric coefficients during cooling were much lower and similar both at 8 MV/m (200V/25mum) and 28 MV/m. They were less than 70 muC/m2K at 95oC and linearly increased with decreasing temperature and they reached the highest value 485 muC/m2K at 65oC. The transition temperature during cooling was hardly affected by the applied electric field. It remained near 65oC both at 8 MV/m (200V/25mum) and 28 MV/m. Subsequent to the above measurements, pyroelectric conversion was examined at various operating conditions using a single 25mum thick 60/40 P(VDF-TrFE) film. A pyroelectric conversion cycle conceived by Olsen was adopted. External control voltage was cycled between high and low in synchronization with cycling of film temperature. When cycled between 700V and 100V and between 30oC and 70oC, electrical output to electrical input ratio reached 1.8. When this ratio is greater than one, it reflects the conversion of heat to electricity through pyroelectric conversion. The net power output density at these conditions before subtracting parasitic losses was 250 J/L of copolymer used. As the difference between high- and low-control voltage increased the electrical output to input ratio also increased. This paper reviews how the pyroelectric effect could be applied to convert heat to electricity and presents experimental results.