Origin of Enhanced Electricity Generation on Magnéli Phase Titanium Suboxide Nanocrystal Films
Pengchao Si,Mengqi Li,Xiang Wang,Feifei Sun,Jingjing Liu,Qinhuan Wang,Fuqiang Ren,Haoran Kong,Yu Wang
DOI: https://doi.org/10.1021/acsaem.1c01840
IF: 6.4
2021-09-20
ACS Applied Energy Materials
Abstract:The energy conversion process caused by relative motion of droplets and nanofilms has aroused widespread attention. However, the mechanism is still unclear, especially regarding the modification of the nanomaterial itself. In this study, we found that by annealing TiO2 in a H2 atmosphere at different temperatures, the Magnéli phase titanium suboxide can be prepared with a lot of oxygen vacancies. Oxygen vacancies not only form negative charge centers inside the film, which enhance the attraction of Na+, but also increase the carrier concentration. By increasing the oxygen vacancy concentration, the measured VOC value was increased by ∼5 times and ISC by ∼30 times. Furthermore, a universal film preparation process was developed for the large-scale production of flexible energy conversion units based on the simple sol–gel method. Experimental results show that the prepared energy conversion unit has excellent performance of collecting rainwater energy and show a stable and continuous VOC output of ∼600 mV, combined with the surface hydrophobic treatment technology.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01840.Element composition and its corresponding quantitative relationship of Ti3C2Tx (Figure S1); element composition and its corresponding quantitative relationship of the freeze-dried PTA gel (Figure S2); digital photos of three different concentrations of PTA gels over time (Figure S3); optical image of a thin film prepared by high viscosity R500 (Figure S4); schematic diagram of the test method for the hydrovoltaic performance of the Magnéli phase film (Figure S5); i–t curves of T800, T900, and T1000 at a constant voltage of 1 V (Figure S6); measured VOC at 126, 246, and 366 h after sample T1000 preparation (Figure S7); resistance test results and VOC test results for films of different thicknesses (Figure S8); XPS survey spectra of T800, T900, and T1000 (Figure S9); high-resolution Ti 2p spectra of T800, T900, and T1000 (Figure S10); VOC of the film tested in six different concentrations of NaCl (Figure S11); VOC of the film tested in HCl solutions with different pH values (Figure S12); measured VOC of the film tested at different flow rates (Figure S13) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels