Photoluminescence of Zn2SiO4 : Mn2+ prepared by combustion technique

Y Hao,YH Wang,ZH Zhang

IF: 4.632

2003-01-01

Journal of Rare Earths

Abstract:Manganese-doped zinc silicate powder samples were prepared successfully by solution combustion process, and their photoluminescence were investigated in ultraviolet region. The single-phase of Zn2-xSiO4 : x Mn (0 less than or equal to x less than or equal to 0.10, willemite) was obtained by combustion synthesis at 600 degreesC for afew minutes, then heat treated at above 900 degreesC for 4 h. In the excitation spectra of Zn2-xSiO4: x Mn (0 < x less than or equal to 0.10), the strongest broad band at about 254 nm is observed and assigned to (6)A(1)-->(4) T-1 transition of Mn2+ monitoring at 525 nm emission. At about 525 nm, the intense broad band emission is observed under 254 nm excitation in Zn2-xSiO4: x Mn (0 < x less than or equal to 0.10). This broad band is attributed to T-4(1)-->(6)A(1) transition of Mn2+. The results indicate that photoluminescence efficiency, the location of the strongest excitation or emission band, and the optimum concentration of activator depend on starting materials, combustion temperatures, the dosage of fuels, and the size of powder samples etc.