Magnetocaloric Effect of Pr 2 Fe 17− X Mn X Alloys
Xi-Chun Zhong,Zhong-Wu Liu,De-Chang Zeng,Karl A. Gschneidner Jr.,Vitalij K. Pecharsky
DOI: https://doi.org/10.1007/s12598-013-0134-x
2013-01-01
Abstract:Polycrystalline Pr2Fe17−x Mn x (x = 0, 1, and 2) alloys were studied by X-ray diffraction (XRD), heat capacity, ac susceptibility, and isothermal magnetization measurements. All the alloys adopt the rhombohedral Th2Zn17-type structure. The Curie temperature increases from 283 K at x = 0 to 294 K at x = 1, and then decreases to 285 K at x = 2. The magnetic phase transition at the Curie temperature is a typical second-order paramagnetic–ferromagnetic transition. For an applied field change from 0 to 5 T, the maximum −ΔS M for Pr2Fe17−x Mn x alloys with x = 0, 1, and 2 are 5.66, 5.07, and 4.31 J·kg−1·K−1, respectively. The refrigerant capacity (RC) values range from 458 to 364 J·kg −1, which is about 70 %–89 % that of Gd. The large, near room temperature ΔS M and RC values, chemical stability, and a high performance-to-cost ratio make Pr2Fe17−x Mn x alloys be selectable materials for room temperature magnetic refrigeration applications.