Abstract:Electrospinning is a simple, versatile technique for fabricating fibrous nanomaterials with the desirable features of extremely high porosities and large surface areas. Using emulsion electrospinning, polytetrafluoroethylene/polyethene oxide (PTFE/PEO) membranes were fabricated, followed by a sintering process to obtain pure PTFE fibrous membranes, which were further utilized against a polyamide 6 (PA6) membrane for vertical contact-mode triboelectric nanogenerators (TENGs). Electrostatic force microscopy (EFM) measurements of the sintered electrospun PTFE membranes revealed the presence of both positive and negative surface charges owing to the transfer of positive charge from PEO which was further corroborated by FTIR measurements. To enhance the ensuing triboelectric surface charge, a facile negative charge-injection process was carried out onto the electrospun (ES) PTFE subsequently. The fabricated TENG gave a stabilized peak-to-peak open-circuit voltage (V-oc) of up to similar to 900 V, a short-circuit current density (J(sc)) of similar to 20 mA m(-2), and a corresponding charge density of similar to 149 mu C m(-2), which are similar to 12, 14, and 11 times higher than the corresponding values prior to the ion-injection treatment. This increase in the surface charge density is caused by the inversion of positive surface charges with the simultaneous increase in the negative surface charge on the PTFE surface, which was confirmed by using EFM measurements. The negative charge injection led to an enhanced power output density of similar to 9 W m(-2) with high stability as confirmed from the continuous operation of the ion-injected PTFE/PA6 TENG for 30 000 operation cycles, without any significant reduction in the output. The work thus introduces a relatively simple, cost-effective, and environmentally friendly technique for fabricating fibrous fluoropolymer polymer membranes with high thermal/chemical resistance in TENG field and a direct ion-injection method which is able to dramatically improve the surface negative charge density of the PTFE fibrous membranes.

The Charge Storage Stability of Porous Polytetrafluoroethy Lene Film Electret

Stability and conductivity study of NH4PO3–PTFE composites at intermediate temperatures

Silicon Based Polytetrafluoroethylene Electrets: Preparation and Corona Charging Characteristics

Percolative Charge Transport on Electrified Surface of Polytetrafluoroethylene

Elaborately fabricated polytetrafluoroethylene film exhibiting superior high-temperature energy storage performance

Electrochemical and X-ray Photospectroscopy Studies of Polytetrafluoroethylene and Polyvinylidene Fluoride in Li/C Batteries

Defects drive the tribocharging strength of PTFE

Stability of cold plasma improved wettability and adhesive property of polytetrafluoroethylene surface

Study of porous dielectrics as electret materials

Electret and Dielectric Properties of Lyophilized Polymer Films

Enhancement of dielectric breakdown strength and energy storage of all-polymer films by surface flattening

Transport Properties of Electro-Sprayed Polytetrafluoroethylene Fibrous Layer Filled with Aerogels/Phase Change Materials

Triphenylamine-triazine polymer materials obtained by electrochemical polymerization: Electrochemistry stability, anions trapping behavior and electrochromic-supercapacitor application

Facile Electrochemical Polymerization of 2-(Thiophen-2-yl)furan and the Enhanced Capacitance Properties of Its Polymer in Acetonitrile Electrolyte Containing Boron Trifluoride Diethyl Etherate

Interfacial and Bulk Polarization of P(VDF-HFP) Investigated by Dielectric Spectroscopy

Triboelectric Polymer with High Thermal Charge Stability for Harvesting Energy from 200 °C Flowing Air

Investigation on the microstructural and mechanical properties of a Polytetrafluoroethylene thin film by radio frequency magnetron sputtering

Etching Processes of Polytetrafluoroethylene Surfaces Exposed to He and He-O2 Atmospheric Post-discharges

Effect of Aging on the Morphology and Wettability of Polytetrafluoroethylene

Creating Ultrahigh and Long‐Persistent Triboelectric Charge Density on Weak Polar Polymer via Quenching Polarization

Emulsion Electrospinning of Polytetrafluoroethylene (PTFE) Nanofibrous Membranes for High-Performance Triboelectric Nanogenerators.