Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system
Hongjie Wang,Zhenying Huang,Xue Li,Qun Yu,Wenqiang Hu,Weici Zhuang,Youbo Wu,Yang Zhou
DOI: https://doi.org/10.1016/j.jallcom.2023.171524
IF: 6.2
2023-07-28
Journal of Alloys and Compounds
Abstract:In the field of exploring the precursors of TiC/Ti composite, Cr 2 AlC was innovatively used as the precursor in this study. Based on the formation of TiC in pure Ti matrix during hot-pressing sintering, Al and Cr elements changed the microstructure of matrix to form TiC/(öÝô +ô öý)-Ti composite, and the reaction mechanism of Cr 2 AlC-Ti system in the sintering process was discussed in detail. During the cooling process, Cr element retained öý-Ti to room temperature, and the uniformly distributed TiC was used as the nucleation site of öÝ-Ti. By controlling the content of Cr 2 AlC added, the microstructure of the composite was regulated. In 10ô vol% Cr 2 AlC/Ti composite, the öÝ-Ti extend form the boundary of TiC to all sides, forming a microstructure of quasi-continuous network structure covering equiaxed öý-Ti, which exhibited the optimal strength with ultimate tensile strength of 1184ô MPa. The interface analysis shown that there is good interface bonding at TiC/öÝ-Ti, which made the whole frame have good load transfer. And there were stacking faults at the TiC/öý-Ti interface, meaning the obvious CTE mismatch strengthening at it.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering