Experimental Research on the Near Net Shape Casting Process of Gamma Titanium Aluminide Turbochargers

Zuojian Liang,Qingyan Xu,Juntao Li,Shiqiong Li,Ji Zhang,Baicheng Liu,Zengyong Zhong

DOI: https://doi.org/10.3321/j.issn:1002-185x.2002.05.009

2002-01-01

Rare Metal Materials and Engineering

Abstract:The research on forming process of gamma titanium aluminide is at the frontier in the field of materials processing. Using water cooling copper crucible, the titanium aluminum alloy was melted by ISM technique, and gamma titanium aluminide turbochargers were produced by centrifugal investment precision casting process. Adopting optimizing design,of risers, sound turbochargers were prepared, and solidification process and shrinkage defects of turbocharger castings were analyzed.. The results showed that shrinkage defects of turbochargers could be decreased or eliminated when the modulus difference between riser and casting or the volume ratio of riser to casting were increased. In order to provide numerical simulation study with thermal property parameters, coefficient of thermal expansion, specific heat and,coefficient of thermal conductivity of the titanium aluminium alloy were measured. The relations between them and temperature could be expressed respectively as: alpha(1) = 8.106 51 + 0.007 3 T - 2.976 19 E - 6T(2); C-P = 668.281 58 - 0. 013T + 1.119 05 E - 4T(2); lambda = 19.822 52 - 0.027 81T + 6.514 97 E - 5T(2) - 3.210 96 E - 8T(3).