Abstract:Ferric pyrophosphate (FePP) was added to an ammonium polyphosphate (APP)-pentaerythritol (petol) intumescent flame retardant (IFR) system in polypropylene (PP) matrix, with subsequent investigation into the synergistic effect between FePP and the IFRs. Limited oxygen index (LOI), UL-94 test and cone calorimeter test were employed to study the flame retardance of the synthesized flame retardant PP composites. Thermogravimetric analysis (TGA) and thermogravimetric analysis-infrared spectrometry (TG-IR) were used to study their thermal degradation characteristics and gas products. TG-IR results demonstrate that there is no Fe (CO)(5) produced from PP/IFR/FePP system, which implies that the flame retardant mechanism of PP/IFR/FePP system is in the condensed phase rather than in the gas phase. Real time FTIR and X-ray photoelectron spectroscopy (XPS) were used to monitor the thermal oxidative stability and the high temperature performance of the flame retardant PP composites. The real time FTIR spectra show that all peaks around 2900 cm(-1) almost disappear at 380 degrees C for the PP/IFR system, meaning that PP decomposes completely at this temperature. But after the addition of 2 wt% wt% FePP, the peaks still exist till 400 degrees C. XPS shows that the aliphatic carbon atom content in PP/23 wt% wt% IFR/2 wt% wt% FePP (63.8%) is much higher than the one without FePP, and the total oxygen atom content in PP/23 wt% wt% IFR/2 wt% wt% FePP is just 19.1%, while the one in PP/25 wt% IFR is as high as 35.7%. Copyright (C) 2009 John Wiley & Sons, Ltd.

Studies on Compatibilization of Intumescent Flame-Retardant/Pp Composites Based on Etched Pp

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Effects of reactive compatibilization on the morphological, thermal, mechanical, and rheological properties of intumescent flame-retardant polypropylene.

Compatibilization of intumescent flame retardant/polypropylene composites based on α-methacrylic acid grafted polypropylene

Polypropylene–intumescent Flame‐retardant Composites Based on Meleated Polypropylene As a Coupling Agent

The Effect of Compatilizer on the Thermal and Mechanical Property of Polypropylene/IFR System

A Study of the Novel Intumescent Flame‐retarded PP/EPDM Copolymer Blends

Study on the Mixture of an Intumescent Flame Retardant Containing Various Caged Phosphates Melamine Salt and PP

Study on PP Flame Retarded with Aryl Phosphate and Intumescent Flame Retardant Compound

Synergistic Effects of Cerium Phosphate and Intumescent Flame Retardant on EPDM/PP Composites

Flame retardant effect of cytosine pyrophosphate and pentaerythritol on polypropylene

Synergistic effect of expandable graphite and intumescent flame retardants on the flame retardancy and thermal stability of polypropylene

Preparation of Efficiently Intumescent-Flame-retarded Polypropylene Composite: Synergistic Effect of Novel Phosphorus-Containing Polyhedral Oligomeric Silsesquioxane

Synthesis of in situ encapsulated intumescent flame retardant and the flame retardancy in polypropylene

Novel Intumescent Flame Retardant Masterbatch Prepared Through Different Processes and Its Application in EPDM/PP Thermoplastic Elastomer: Thermal Stability, Flame Retardancy, and Mechanical Properties

Synergistic effects of ferric pyrophosphate (FePP) in intumescent flame-retardant polypropylene

Using PA6 As a Charring Agent in Intumescent Polypropylene Formulations Based on Carboxylated Polypropylene Compatibilizer and Nano‐montmorillonite Synergistic Agent

Great enhancement of efficiency of intumescent flame retardants by titanate coupling agent and polysiloxane

Research Progress on the Compatibility Improvement of Polypropylene Flame-retarded by Intumescent Flame Retardants

Intumescent Flame Retardation and Silane Crosslinking of PP/EPDM Elastomer