Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Investigation of the Corrosion Products Formed on Carbon Steels Pre-Corroded by Different Gaseous Pollutants

EFFECT OF THE DIFFERENT PRE-RUSTED METHODS ON THE ATMOSPHERIC CORROSION BEHAVIOR OF CARBON STEEL

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Characterization of the rust on carbon steels pre-corroded by different gaseous pollutants

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Influence of Cl- and SO2 on Carbon Steel Q235, Pipeline Steel L415 and Pressure Vessel Steel 16MnNi Corrosion Behavior in Industrial and Marine Atmosphere Environment

Study on rust layers of carbon steel, weathering steel and alloy steel exposed to Shanghai atmosphere for three years

Atmospheric Corrosion of Steel A3 Deposited with Ammonium Sulfate and in the Presence of Sulfur Dioxide

Effect of Exposure Time on the Corrosion Rates of X70 Steel in Supercritical CO2/SO2/O2/H2O Environments

Comparative study of alternating dry and wet corrosion behavior of Q345qDNH steel and Q420qENH steel in industrial atmospheric media containing PM2.5

Corrosion Of Carbon Steel In Typical Water Environments Of Thermal Power Plant

Corrosion Electrochemical Behavior of 20 Steel and 16Mn Steel in Simulated CO2 Flooding Environment

Corrosion behaviors of steels under supercritical CO2 conditions

Corrosion Behavior of J55 and N80 Carbon Steels in Simulated Formation Water under Different CO2 Partial Pressures

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Prediction of Tempo-Spatial Patterns and Exceedance Probabilities of Atmospheric Corrosion of Q235 Carbon Steel Across China

Failure analysis of corrosion products formed during CO2 pre-corrosion of X70 and 3Cr steels: Effect of oxygen contamination

Corrosion of Six Steel Materials in Typical Industry Atmosphere

Corrosion evolution of electric power equipment metal materials under industrial pollution environment with high heat and high humidity