Abstract:The purpose of this study was to assess the effects of different aqueous environments (i.e., demineralised, distilled and spring water) on the mechanical properties of a cold-cured bisphenolic epoxy resin modified with the addition of calcium carbonate filler, typically employed as structural adhesive. The parameters selected for the analysis have been; the kind of curing agent employed to cure the epoxy resin at ambient temperature (i.e., Mannich base and triethylenetetramine); the load of calcium carbonate added to liquid epoxy (i.e., from 1 to 3 g per 100 g of resin) and; the duration of the exposure to the different aging conditions (i.e., from 1 to 10 months). Cylindrical specimens of calcium carbonate-modified epoxy systems were tested in compression mode, before and after each of the aging regimes. The effect of the selected curing agents is very small, and they are both suitable for a cure at ambient temperature, on the unfilled epoxy on compressive maximum strength and strain at break; the choice of the hardener affects instead the compressive modulus. The CaCO3 amount was demonstrated to have a significant effect on the mechanical characteristics of un-aged epoxy systems, leading to growth in compressive modulus and maximum strength with reductions in strain at break. Generally speaking, the aging time noticeably affects the compressive properties of calcium carbonate-modified epoxies while almost negligible is the kind of water employed in each exposure regime. Notwithstanding the adverse effects of an aqueous environment on compressive mechanical properties of CaCO3-filled epoxies, these systems keep compressive modulus and maximum strength greater than, and close to, respectively, the same characteristics measured on unaged unfilled control epoxies, demonstrating the positive effect of the addition of this kind of filler to epoxy-based structural adhesives, especially with the addition of 2 and 3 g of CaCO3 per 100 g resin. The results obtained in this study demonstrated that it is possible to contrast the detrimental effects observed in cold-cured epoxy-based structural adhesives due to their aging in water upon the addition of limited amounts (particularly at 2 and 3 g per 100 g resin) of a cheap CaCO3 filler.

EFFECTS OF HYDROTHERMAL AGEING ON STRUCTURES AND PROPERTIES OF CYANATE/EPOXY NOVOLAC BLENDS

Study on Co-curing Behavior and their Laminate Properties of Low Bromined Epoxy/Cyanate Blends

Contributions of Side Groups to the Water Diffusion in Cured Epoxy Resins (2) Study on Physical Aging

Curing, Thermal Stability and Composite Properties for Blends of the Novel Bismaleimide and Cyanate Containing Naphthalene

Nonisothermal Reaction, Thermal Stability and Dynamic Mechanical Properties of Epoxy System with Novel Nonlinear Multifunctional Polyamine Hardener

Thermal properties of an epoxy cresol-formaldehyde novolac/diaminodiphenyl sulfone system modified by bismaleimide containing tetramethylbiphenyl and aromatic ether structures

Chemical, mechanical and morphological investigation on the hygrothermal aging mechanism of a toughened epoxy

The hygrothermal aging process and mechanism of the novolac epoxy resin

Effect of Decabromodiphenylethane on the Thermo-Oxidative Ageing Property of Epoxy Resin

Accelerated ageing due to moisture absorption of thermally cured epoxy resin/polyethersulphone blends. Thermal, mechanical and morphological behaviour

Effects of Hygrothermal and Salt Mist Ageing on the Properties of Epoxy Resins and Their Composites

Study of E-51 Epoxy Resin Modified Bisphenol A Cyanate Ester Resins

Aging Effects of Aqueous Environment on Mechanical Properties of Calcium Carbonate-Modified Epoxy Resin

Enhanced Interfacial, Mechanical, and Anti-Hygrothermal Properties of Carbon Fiber/cyanate Ester Composites with the Catalytic Sizing Agents of Titanium Epoxy

Effect of Structure of Bridging Group on Curing and Properties of Bisphenol-A Based Novolac Epoxy Resins

Preparation, Curing Properties, and Phase Morphology of Epoxy-Novolac Resin/multiepoxy-Terminated Low-Molecular-weight Poly(phenylene Oxide) Blend

Morphology and mechanical properties of poly(ether-imide)-modified polycyanurates

Investigation on Thermal and Dimensional Stability of Epoxy Resin In-Situ Modified by Cyanate Ester Resin and Polydimethylsiloxane

Effect of curing agents n‐octylamine and m‐xylene diamine on the mechanical and memory properties of E51 epoxy resin

Effects of hygrothermal and thermal-oxidative ageing on the open-hole properties of T800/high-temperature epoxy resin composites with different hole shapes

Effects of Moisture Ingress on the Mesoscale Mechanical Properties of Epoxy Adhesives under Elevated Temperature