Analysis of Microstructure in the Interface of Diffusion Welding for Fe3Al/Q235 Dissimilar materials

李亚江,王娟,尹衍升,吴会强,冯吉才

DOI: https://doi.org/10.3321/j.issn:0253-360X.2002.02.007

2002-01-01

Abstract:Phase structure characteristics nearby the interface of Fe3Al/Q235 diffusion welding are researched by X-ray diffraction (XRD) and transmission electronic microscope (TEM), etc. The test results indicated that obviously diffusion transition zone forms nearby the interface of Fe3Al/Q235 under the condition of heating temperature 1050-1080°C ,holding time 60 min and pressure 9.8 MPa, which indicated that the diffusion interface of Fe3Al/Q235 was combined well. The diffusion transition zone consists of Fe3Al and α-Fe (Al) solid solution. Microhardness in the diffusion transition zone nearby is HM 480-540. There is not brittle phase of high hardness in the interface transition zone. This is favorable to enhance toughness of Fe3Al/Q235 diffusion welded joint. There is crystal oriental relation of (110̄)α-Fe(Al)//(011)Fe3Al and [001]α-Fe(Al)//[100]Fe3Al between Fe3Al phase and α-Fe (Al) solid solution in the diffusion transition zone.