Abstract:In this study, the oxygen evolution kinetics and oxide layer properties of Pb–0.8%Ag rolled-alloy anodes were investigated during 15d of galvanostatic electrolysis in an acidic zinc sulfate electrolyte solution containing 600mg·L−1 Cl− ions. Cyclic voltammetry, quasistationary polarization, and electrochemical impedance spectroscopy were used to investigate the anode process. The microscopic morphology and phase composition of the anodic oxide layers were observed by scanning electron microscopy and X-ray diffraction, respectively. The observable variations in the electrocatalytic activity and reaction kinetics of the anodes during electrolysis indicate the formation and stabilization of the anodic oxide layer. With prolonged electrolysis, the oxygen evolution overpotential in the anodes mainly exhibited a decreasing trend, which is contrary to the trend of the electrode surface exchange current density. This depolarization may have been caused by the increasing roughness of the anodic surface and the catalytic effects of α-PbO2 and β-PbO2. As electrolysis continued, the cathodic peak (α-PbO2→PbSO4) mainly showed an increasing trend and gradually moved toward the negative direction. After 15days of electrolysis, the oxide layers exhibited a severely corrosive microstructure with plenty of cavities and etch pits. The uniform, well-defined crystal grains and regularity were not appeared. The phase composition of the anodic oxide layer was formed after 6d of electrolysis. α-PbO2 proved to be the main peak and showed preferential growth orientations along the (111) planes of the anodic oxide layer.

The cathodic reduction process of the anodic Pb(II) oxides film formed on lead

A study of the reduction process of anodic PbO2 film on Pb in sulfuric acid solution

Analysis of the Oxidation Process of Anodic Pb(II) Films on Lead in Sulfuric Acid Solution

Reduction of Anodic Lead Sulfate Film on Lead in Sulfuric Acid Solution

The growth mechanism of the anodic Pb(II) film formed on lead-tin alloy in sulfuric acid solution

The Mechanisms for the Growth of the Anodic Pb(II) Oxides Films Formed on Pb–Sb and Pb–Sn Alloys in Sulfuric Acid Solution

Oxidation Kinetics of A Lead Electrode Covered with an Anodic Pb-(Ii) Film in Sulfuric Acid Solution

The Growth Mechanism of the Anodic Pb (double-struck I sign) Film Formed on Lead-tin Alloy in Sulfuric Acid Solution

Comparison of the reduction behaviour of anodic PbO2 films on Pb-As and Pb-Bi alloys in sulfuric acid

Effect of Antimony on the Reduction of Anodic Pbo2 Film on Pb-Sb Alloys in Sulfuric Acid Solution

Resistance of the Anodic Pbo Film Formed in Sulfuric Acid Solution

Properties of Anodic Pb(Ⅱ) Film Formed on Lead-Bismuth Alloy

Effects of Samarium on the Properties of the Anodic Pb(Ii) Oxides Film Formed on Pb in Sulfuric Acid Solution

Problems on the Study of Anodic Films on Pb in Sulfuric Acid Solution(Ⅰ)

Electrochemical Behavior of Rolled Pb–0.8%Ag Anodes in an Acidic Zinc Sulfate Electrolyte Solution Containing Cl− Ions

The Effect of Samarium Replacing Calcium on the Anodic Behavior of Lead Alloy in Sulfuric Acid Solution

Transformation of Inert PbSO4 Deposit on the Negative Electrode of a Lead-Acid Battery into Its Active State

Investigation on properties of anodic corrosion films formed on Pb-Ce and Pb-Ca-Sn alloys

Impedance Study of the Anodic Pb(II) Film Formed on Pb-Gd and Pb Electrodes in Sulfuric Acid Solution

Study on the reversibility of PbOx(1<<2)/Pb2+ in different electrolytes containing CH3SO3−, CF3SO3−, and ClO4− for soluble lead flow batteries

The anodic films on lead alloys containing rare-earth elements as positive grids in lead acid battery