Abstract:The immobilized TiO2 nanobelts (NBs) were prepared by anodization and calcined at different temperatures in air. The influence of calcination temperature on the crystallinity, crystal phase and crystallite size were investigated using X-ray diffraction (XRD). The XRD analysis showed that the as-prepared specimen without calcination was completely amorphous and the crystallinity was improved as enhancing the calcination temperature. The crystalline structure of the samples calcined at 350,450 and 550 degrees C was pure anatase phase. A phase transition to rutile phase occurred at 650 degrees C. The crystallite size of TiO2 NBs increased as increasing calcination temperature except for 650 C. Experimental results revealed that the optical, photoelectrochemical and photocatalytic properties of TiO2 NBs were significantly affected by the calcination temperature. The charge transfer and separation efficiency increased gradually with increasing the calcination temperature from 350 to 550 degrees C and then decreased at 650 and 750 degrees C. The photocatalytic activity was assessed by detecting the formation of hydroxyl radicals and photocatalytic degradation of dye rhodamine B. Accordingly, the sample calcined at 550 degrees C showed the highest photocatalytic performance, which is a combined result of appropriate crystallinity, crystal phase, crystallite size and impurity doping. Furthermore, the prepared samples were applied to remove antibiotic amikacin from aqueous solution under simulated sunlight irradiation. Approximately 70% of amikacin was decomposed after irradiation of 150 min for the TiO2 NBs calcined at 550 degrees C, and the photocatalytic degradation of amikacin fits pseudo first-order kinetics. This work indicates that the calcination temperature is an important parameter by which the activity of TiO2 nano catalysts can be tailored. (C) 2013 Elsevier Ltd. All rights reserved.

Effect of the calcining temperatures on the properties of nanocrystalline TiO2

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

TiO2 Nanobelts – Effect of Calcination Temperature on Optical, Photoelectrochemical and Photocatalytic Properties

Effects of calcination on the photocatalytic properties of nanosized TiO2 powders prepared by TiCl4 hydrolysis

Transition of TiO 2 in TiO 2 /vermiculite Nanocomposites

The Calcination Effect on the Crystallinity, Nitrogen Content, and Pore Structure of Nitrogen-Doped Titanium Dioxide

Structure Transition of Nano-Titania During Calcination

Effect of Calcination Temperature on Morphology and Photocatalytic Activity of Anatase TiO2 Nanosheets with Exposed {0 0 1} Facets

Investigation on technological process of preparation of TiO2 nanocrystal for rutile crystal growth

Effect of Calcination Temperature on the Catalytic Activity of Nanosized TiO2 for Ozonation of Trace 4-Chloronitrobenzene

Effect of Calcination Temperature on the Structure, Crystallinity, and Photocatalytic Activity of Core-Shell SiO2@TiO2 and Mesoporous Hollow TiO2 Composites

Effect of Calcination Temperature on Photocatalytic Activity of Synthesized TiO2 Nanoparticles via Wet Ball Milling Sol-Gel Method

Preparation of TiO2 Nanofibres and Influence of Calcination Temperature on Photocatalytic Activity

Synthesis and characterization of nanosized anatase TiO2 cuboids

The Effect of Calcination Conditions on the Morphology, the Architecture and the Photo-Electrical Properties of Tio2 Nanotube Arrays

Effects of Calcination Condition on the Structure and Denitrification Performance of NiO/TiO_2 Catalyst

The Effect of Calcination Temperature on the Structure and Performance of Nanocrystalline Mayenite Powders

Study on Phase Transition of Nano-Size TiO2 During the Heat Treatment

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase