Phase Forming and Development of Multi-Phase Polymer Systems During Melting - Sem Pattern Analysis of Polystyrene/Poly (Cis-Butadiene) Rubber Immiscible Blends

XB Yuan,J Sheng,XZ Li,JS Li,ZJ Cai

2001-01-01

Abstract:The phase forming and development of polystyrene/poly( cis-butadiene) rubber (weight ratios were 70/30 and 50/50, respectively) blends during mixing were investigated by pattern analysis of scanning electron microscope. For the blend with composition 70/30, the average diameter (PDav) of the dispersed phase [particles (PcBR)] decreased in the initial stage of mixing, and fluctuated in the metaphase and later stage. The distribution of the particles trended to uniform with the blending process. But for the blend with composition 50/50, which is near the phase inversion composition, the calculation of PDav is difficult because of the co-continuous structure of the two components, thus two parameters, the characteristic length Lambda and the average characteristic length Lambda (m) are used to characterize the size of the dispersed phase. The characteristic length was defined as the measuring distance of black area (dispersed phase) when scanned the binarized SEM images along a direction. The changes of Lambda (m) was similar to that of PDav, and the Lambda and Lambda (m) could reflect the size and size distribution of the dispersed phase whether or not the composition is near the phase inversion. Furthermore, the histograms of Lambda (m) obtained at various time in the metaphase and later stage of mixing fell on a master curve, demonstrating the self-similar growth of the phase structure. Thus a scale function P (Lambda/Lambda (m)) was defined to study the fractal. behavior of the mixing. The results showed that the fractal dimension D could be used to characterize the mixing process of the polymer blend.