Crystal structure and electrochemical properties of La(Ni,Sn)5+x (x=0～0.35) hydrogen storage alloys
WEI Fan-song,LEI Yong-quan,LU Guang-lie,ZHENG Yao-wu,LY Shou-quan
DOI: https://doi.org/10.3785/j.issn.1008-973X.2007.08.030
2007-01-01
Abstract:The effect of stoichiometric ratio on the crystal structure and electrochemical properties of Co-free La(Ni,Sn)5+x(x=0~0.35) alloys was systematically studied.x-ray diffraction(XRD) analysis shows that all the alloys are single-phase with CaCu5-type structure.In the CaCu5-type structure of over-stoichiometric(x0) alloys,La atoms on 1a sites are partially substituted by the dumbbell pairs of Ni atoms aligned along the c axis,and the fraction of Ni-Ni dumbbells increases with the increase of x value,which leads to a noticeable increase in the c axis and the c/a ratio but a decrease in the cell volume,and also leads to a noticeable decrease in volume expansion rate of the alloys on hydriding.Electrochemical test shows that with the increase of x,the cycling stability of the alloys is greatly improved,while the maximum discharge capacity and high-rate dischargeability of the alloys are somewhat lowered.The increase of stoichiometric ratio of the alloys leads to a larger fraction of Ni-Ni dumbbells in their structure,and improves greatly the pulverization resistance of the alloys on hydriding,and then decreases the reaction surface area of the alloy particles during cycling,which leads to higher corrosion resistance and improved cycling stability.But the decrease of the reaction surface area of the alloys also lowers the electrode reaction rate,resulting in a lower high-rate dischargeability.