Experimental investigation on the inhomogeneities of transverse microstructure and internal stress of high‐strength low‐alloy hot‐rolled strip
Aigeng Fei,Wenguang Wang,Xiaohe Yang,Rundong Xue,Jiaojian Ai,Zhiyi Zhao
DOI: https://doi.org/10.1002/srin.202200162
IF: 2.1258
2022-11-12
steel research international
Abstract:In this paper, the evolution of transformation in the width direction of high‐strength low‐alloy hot‐rolled strip was studied by using thermo mechanical simulation, and the temperature, microstructure, and internal stress were correlated based on Electron Backscatter Diffraction (EBSD) data. The temperature and time range of the transverse transformation were determined based on the thermal expansion curve. The results show that the transformation at the edge of the steel plate ended earliest and that at the plate center began at the latest; only 31.9 % austenite underwent transformation at the plate central by the end of laminar cooling. The fraction of transformed austenite at the plate center was the least throughout the laminar cooling process. The proportion of small grains (within the grain size range of 0 to 4 μm), mean and variant coefficient of grain sizes at the plate edge are 75 %, 4 μm, and 1.29, respectively. In contrast, those values of the central region are 66 %, 4.4 μm, and 1.05, respectively. The correlation between temperature and internal stress evolutions is established. It is demonstrated that the internal stress increases monotonically with the average transformation rate. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering