Abstract:This study aimed to enhance the sinterability and conductivity of yttria fully stabilized zirconia electrolyte through co-doping by 2 mol% of ZnO and different contents of MnO 2 (0, 0.5, 1, 1.5 mol%) at two sintering temperatures of 1300 and 1400 °C. Phase composition identification, density, microstructure, and conductivity of the samples were evaluated using X-ray diffraction (XRD), Archimedes' method, field emission scanning electron microscopy (FESEM), and electrochemical impedance spectroscopy (EIS), respectively. The XRD results revealed that ZnO and MnO 2 are successfully doped in the fluorite structure of YSZ sintered at 1400 °C, and the cubic structure is completely preserved. However, at a sintering temperature of 1300 °C, the (111) peaks of doped samples were slightly split, which implied a slight phase transformation of YSZ from cubic to a tetragonal structure. The co-doped samples, at both sintering temperatures, showed higher relative density and grain size compared with pure YSZ. The addition of 2 mol% of ZnO and 0.5 mol% of MnO 2 at 1400 °C increased the relative density of YSZ from 81.6% to 95.1%. The increase in relative density and grain size, while maintaining the cubic structure, caused an increase in the conductivity of the mentioned sample. Compared with pure YSZ, the sample's total conductivity increased from 7.37 to 10.03 S m −1 at 800 °C. The proposed composition showed better sintering behavior, lower activation energy of grain conductivity, and higher conductivity than pure YSZ. This behavior is thought to be due to the facilitating rearrangement of atoms during sintering and an increase in oxygen ion vacancy concentration due to co-doping with the appropriate amount of ZnO and MnO 2 .

Conductivity of Y2O3 and Yb2O3 co-doped zirconia materials in the intermediate and low temperature range

Low-temperature ionic conductivity of the solid solution in the system ZrO2–Y2O3–Yb2O3

Temperature-dependence of the lattice conductivity of mixed calcia/yttria-stabilized zirconia

Temperature dependence of the ionic conductivity for yttria-stabilized zirconia

Low Thermal Conductivity Without Oxygen Vacancies in Equimolar YO1.5 + TaO2.5- and YbO1.5 + TaO2.5-stabilized Tetragonal Zirconia Ceramics

Analysis of the ionic conduction in Y2O3-stabilized ZrO2 at low temperatures by impedance spectroscopy

Ionic conduction in cubic zirconia at low temperatures

Thermal Conductivity of Ytterbia-Stabilized Zirconia

Activation Energy for Conduction in Y2o3-Stabilized Zirconia

Ionic conductivity in the ternary system (ZrO2)1−0.08 x −0.12 y –(Y2O3)0.08 x –(CaO)0.12 y

Electrical Conductivity of Mixed Conductors (Yo<sub>1.5</sub>)<sub>x</sub>-(Ceo<sub>2</sub>)<sub>y</sub>-(zro<sub>2</sub>)<sub>1-x-y</sub>

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Effect of lattice defects on thermal conductivity of Ti-doped, Y 2O3-stabilized ZrO2

Grain-Size Dependence of the Grain-Boundary Conductivity of Zirconia Stabilized by Y2O3 and CaO

Ionic Conduction in Cubic Zirconias at Low Temperatures

Electrical conductivity of mixed conductors (YO1.5) x.(CeO2)y.(ZrO2)1-x-y

Effect Of Bismuth Oxide On The Microstructure And Electrical Conductivity Of Yttria Stabilized Zirconia

Evidence of non-linear relationship between the electrical conductivity of Y2O3-stabilized-ZrO2 in the low temperature range

Conductivities in Yttrium-Doped Barium Zirconate: A First-Principles Study

Influence of doping elements on thermo-physical properties of co-doped strontium zirconate for potential thermal barrier coatings