Synthesis of Nanometer-Sized Mesoporous Oxide Spheres

Q Luo,L Li,ZY Xue,DY Zhao

IF: 3.1

2001-01-01

Chemical Research in Chinese Universities

Abstract:A few hundreds nanometer-sized mesoporous silica and alumina spheres were synthesized in organic solvents. The impacts of ammonia, N, N-dimethylformamide (DMF) and stirring speed were also investigated.

What problem does this paper attempt to address?

Synthesis of Nanometer-sized Mesoporous Silica and Alumina Spheres

Qian Luo,Li,Zhiyuan Xue,Dongyuan Zhao

DOI: https://doi.org/10.1016/s0167-2991(00)80194-9

2000-01-01

Abstract:Mesoporous silica and alumina spheres with a few hundred nanometer-sized have been synthesized in the presence of the organic solvent with aqueous ammonia as the morphological catalyst. Mesoporous silica spheres templated by the cationic surfactant cetyltrimethylammonium bromide (C.TAB) show hexagonal mesostructure with monodispersed pore sizes ( 2.4 nm) and high surface areas (~ 1020 m2/g) similar to MCM-41. The diameter sizes (80800 nm) of the silica spheres can be tunable by changing the ratio of water to N,N-dimethylformamide (DMF) and ammonia concentration in the solution. A large pore mesoporous alumina sphere templated by amphiphilic triblock copolymer has nanometer size range of 100900 nm and is thermally stable. Calcined alumina sphere shows disordered mesoporous arrays with pore size of 10 nm and high surface areas ( 360 m2/g).
Synthesis of Mesoporous Silica Spheres by Using Neutral-cationic Surfactant and Semi-batch Growth

JQ Qiu,X Zhao,MC Jin,Q Cai,HD Li

DOI: https://doi.org/10.3321/j.issn:1000-324x.2006.03.008

2006-01-01

Abstract:A one-step synthesis of mono-dispersed mesoporous silica spheres by using the mixed surfactants CTAB and dodecylamine proceeded with the hydrolysis and condensation of tetraethylorthosilicate (TEOS) in a mixture of alcohol, isopropyl alcohol, water, and ammonia as a catalyst. The silica spheres have high specific surface area and can be used as a good substrate in high performance liquid chromatography (HPLC). The size of 0.2 similar to 1.5 mu m and morphology of the silica spheres can be controlled by varying the proportion of surfactant and co-solvent. The prepared silica spheres can be enlarged to the maximum diameter 3 mu m with a seeded growth method in a semi-batch reacting system. Based on the experiments above, several mechanisms were discussed on the growth process of mesoporous silica spheres in the synthesis.
Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

Xiao Wei,Gang Xu,Zhaohui Ren,Yonggang Wang,Ge Shen,Gaorong Han

DOI: https://doi.org/10.1111/j.1551-2916.2007.02015.x

IF: 4.186

2008-01-01

Journal of the American Ceramic Society

Abstract:Monodisperse porous SrTiO3 spheres with an average size of ca. 200 nm were synthesized via a hydrothermal route in the presence of poly vinyl alcohol (PVA). Characterization techniques such as X‐ray diffraction, scanning electron microscopy, transmission electron microscopy, SAED, and high‐resolution transmission electron microscopy were used to investigate the products. The results showed that these porous spheres were compared of small primary nanocrystals and pores were formed among them. The nanocrystal and pore diameters increased as the reaction time proceeded. It was suggested that the PVA played an important role in the mesoporous sphere's formation by means of preventing nanocrystal growth through a capping effect.
One-pot Template-Free Synthesis of Mesoporous Boehmite Core–shell and Hollow Spheres by a Simple Solvothermal Route

Liangmiao Zhang,Wencong Lu,Rongrong Cui,Shanshan Shen

DOI: https://doi.org/10.1016/j.materresbull.2009.11.010

IF: 5.6

2010-01-01

Materials Research Bulletin

Abstract:Uniform-sized and monodispersed boehmite core–shell and hollow spheres have been successfully synthesized using a template-free solvothermal route. The experimental parameters such as reaction duration, the trisodium citrate amounts and solvents are shown to play important roles in the formation of the AlOOH core–shell and hollow spheres. X-ray diffraction, Fourier transform IR, thermal gravimetric analysis, N2 adsorption/desorption, scanning electron microscopy, transmission electron microscopy, and high-resolution TEM were used to characterize the products. The results show that the prepared polycrystalline hollow spheres are composed of well-aligned AlOOH nanowires and have an orthorhombic structure. Finally, a dissolution–renucleation mechanism was proposed for the formation of boehmite hollow structures.
Synthesis of Novel Mesoporous Silica Spheres with Starburst Pore Canal Structure

YB Zhang,XF Qian,ZK Li,J Yin,ZK Zhu

DOI: https://doi.org/10.1016/j.jssc.2003.09.018

IF: 3.3

2004-01-01

Journal of Solid State Chemistry

Abstract:Novel spherical mesoporous silica materials with uniform diameters and starburst mesopore structures were synthesized by a simple one-step procedure with ethanol as the co-solvent in dilute aqueous solution and their formation mechanism was proposed. The arrangement of the pore canal and the diameter of the sphere could be tailored by altering the concentration of ethanol.
Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

J Lei,CZ Yu,J Fan,Y Yan,B Tu,DY Zhao

DOI: https://doi.org/10.3321/j.issn:0567-7351.2005.08.014

2005-01-01

Acta Chimica Sinica

Abstract:A new procedure for the synthesis of mesoporous silica spheres with controlled particle size (9.0 similar to 17.6 mu m) and pore size (2.3 similar to 4.8 nm) was developed. It was based on the hydrothermal syntheses by mixing nonionic surfactant EP20PO30EO20 (P65) and TEOS under static acidic conditions. The size of spheres was controlled by adjusting the synthesis temperature, the synthesis time, and the amount of added KCl. The pore size of the spheres was controlled by adding the 1,3,5-trimethylbenzene (TMB) or changing the hydrothermal. temperature and characterized by nitrogen adsorption-desorption analysis, whereas the size of the spheres was analyzed by scanning electron microscopy (SEM) and further confirmed by the laser scattering particle size distribution analyzer. The bio-immobilization ability of such mesoporous silica spheres was characterized by protein adsorption analysis. Mesoporous silica spheres with the largest pore size (4.8 nm) among all materials under investigation showed the highest specific immobilization amount of lysozyme (192 mg/g), while the spheres with smaller pore size (<= 4.3 nm) have markedly low immobilization amount (<= 42 mg/g). These mesoporous silica spheres with diameter similar to 10 mu m in size may be readily used as a good substrate in high performance liquid chromatography (HPLC).
Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Xueling Zhang,Weiyao Zhu,Mengjing Cao,Qiang Cai,Xiaofeng Wang,Yu Lou

DOI: https://doi.org/10.4028/www.scientific.net/amm.448-453.154

2014-01-01

Abstract:Size-controllable synthesis of worm-like microporous monodispersed SiO2microspheres using dodecylamine (DDA) as direct agent in ethanol-water solvent system was firstly developed by varying the proportion of reactants. The products were characterized with scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), small angle X-ray diffraction (SAXRD) and nitrogen adsorption. The results showed that the SiO2microspheres with size of 50nm~1um could be prepared by varying the molar ratio of water/ethanol when the molar ratio of (DDA)/tetraethyl orthosilicate (TEOS) is 0.4 and the concentration of TEOS varied from 0.138 to 0.248mol/L. This method is simple and convenient, the prepared SiO2microspheres are monodispersed and uniform, the worm-like pore size is about 1.4nm. The size controllable silica microspheres could be used as an excellent additional medium to alter rheological behavior of fluid after surface modification..
Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Nan Yao,Guoxing Xiong,King Lun Yeung,Shishan Sheng,Mingyuan He,Weishen Yang,Xiumei Liu,Xinhe Bao

DOI: https://doi.org/10.1021/la0116084

IF: 3.9

2002-01-01

Langmuir

Abstract:A novel sol−gel process has been developed for the synthesis of amorphous silica−aluminas with controlled mesopore distribution without the use of organic templating agents, e.g., surfactant molecules. Ultrasonic treatment during the synthesis enables production of precursor sols with narrow particle size distribution. Atomic force microscopy analysis shows that these sol particles are spherical in shape with a narrow size distribution (i.e., 13−25 nm) and their aggregation during the gelation creates clusters containing similar sized interparticle mesopores. A nitrogen physiadsorption study indicates that the mesoporous materials containing different Si/Al ratios prepared by the new synthesis method has a large specific surface area (i.e., 587−692 m2/g) and similar pore sizes of 2−11 nm. Solid-state 27Al magic angle spinning (MAS) NMR shows that most of the aluminum is located in the tetrahedral position. A transmission electron microscopy (TEM) image shows that the mesoporous silica−alumina consists of 12−25 nm spheres. Additionally, high-resolution TEM and electron diffraction indicate that some nanoparticles are characteristic of a crystal, although X-ray diffraction and 29Si MAS NMR analysis show an amorphous material.
Synthesis of monodispersed mesoporous silica spheres (MMSSs) with controlled particle size using gemini surfactant

Qianru Chen,Lu Han,Chuanbo Gao,Shunai Che

DOI: https://doi.org/10.1016/j.micromeso.2009.08.024

IF: 5.876

2010-01-01

Microporous and Mesoporous Materials

Abstract:A series of mesoporous silica spheres with tunable particle size were synthesized by the self-assembly of cationic gemini surfactant and silica source under basic condition. By varying the initial synthesis conditions, such as molar composition, temperature and addition of co-solvent, the particle sizes of the MMSSs with radially oriented pore structure were controlled in a range of 120–490nm, and the pore sizes changed from 2.2 to 3.4nm. The MMSSs have been obtained under different conditions when ethanol was used as co-solvent. With increasing the concentration of ethanol, the sphere diameter varied from 70 to 460nm. The increasing of reaction temperature from 0 to 90°C led to the average diameter of the mesoporous silica spheres changing from 90 to 410nm. Higher NaOH concentration and lower surfactant concentration have been found to facilitate the formation of MMSSs with larger particle size. MMSSs with diameter of 180–380nm were also synthesized with the addition of the co-solvents such as isopropanol, acetone, acetonitrile, dimethyl sulfoxide and methanol. The possible mechanism responsible for the shape and structure of MMSSs was discussed.
Preparation of Nano-Sized Mesoporous Silica Dioxide and Al-Doped Silica Dioxide at Extremely Low Reactant Concentration

Cheng Hong-Yun,Shi Yan-Tao,Nan Hai-Ming,Geng Yi,Chen Bao-Hua,Cai Qiang

DOI: https://doi.org/10.3321/j.issn:0251-0790.2009.06.001

2009-01-01

Abstract:Syntheses of nano-sized mesoporous silica dioxide and that with Al doped were preformed at extremely low reactant concentration, and the products were controllable in size (20-70 nm), morphology and pore structure by changing the amount of deionized water or Al source in the reaction. The samples were of high BET surface area( more than 1000 m(2)/g) and pore volume (1.1-1.8 cm(3)/g). The pore structure became less ordered, the particle size decreased, the pore volume increased and a certain accumulation of holes appeared when decreasing reactants concentration or introducing Al source in the reaction. The nano-sized mesoporous samples were characterized by transmission electron microscopy (TEM), small-angle X-ray diffraction, and nitrogen adsorption/desorption techniques.
Synthesis of micrometer-sized hard silica spheres with uniform mesopore size and textural pores

L.M. Yang,Y.J. Wang,Y.W. Sun,G.S. Luo,Y.Y. Dai

DOI: https://doi.org/10.1016/j.jcis.2006.02.043

IF: 9.9

2006-01-01

Journal of Colloid and Interface Science

Abstract:Micrometer-sized silica spheres were prepared using a new pH-induced rapid colloid aggregation method in water-in-oil (W/O) emulsion separately with F127 and the mixture of Pluronic triblock copolymer (F127, P123, or P105) and PEG20000 as templates. All the mesoporous silica spheres exhibited high surface areas (657–1145 m2/g) and large pore volumes (0.46–2.16 ml/g). Through optimizing the synthetic conditions, hard silica spheres with narrow particle size distribution, uniform pore size, and textural pores were obtained. Finally, the mechanism of this synthetic route is discussed.
The Size-Controllable Synthesis of Nanometer-Sized Mesoporous Silica in Extremely Dilute Surfactant Solution

Yan-Tao Shi,Hong-Yun Cheng,Yi Geng,Hai-Ming Nan,Wei Chen,Qiang Cai,Bao-Hua Chen,Xiao-Dan Sun,You-Wei Yao,Heng-De Li

DOI: https://doi.org/10.1016/j.matchemphys.2009.10.045

IF: 4.778

2010-01-01

Materials Chemistry and Physics

Abstract:10-60 nm-sized mesoporous silica particles with ordered or worm-like pore structures were controllably synthesized in extremely dilute surfactant solution, and the lowest concentrations of TEOS and CTAB were 12.45 mK 1.52 mM, respectively. The synthesis of nanometer-sized Al-incorporated mesoporous silica particles (Al-MS) was also performed under the similar conditions. Compared to the mesoporous silica without doping of aluminum, those Al-incorporated silica particles have a certain textural mesoporosity. The results indicate that the size and pore structure of mesoporous silica can be adjusted by changing the concentration of reactants. The mesoporous silica nanoparticles, including AI-MS, were characterized by transmission electron microscopy (TEM), small-angle X-ray diffraction (SAXRD), as well as nitrogen adsorption/desorption techniques. It was suggested that the formation of the mesoporous silica nanoparticles could be attributed to the deposition of self-assembled silicate micelles. (C) 2009 Elsevier B.V. All rights reserved.
Micrometer-Sized Mesoporous Silica Spheres Grown under Static Conditions

LM Qi,JM Ma,HM Cheng,ZG Zhao

DOI: https://doi.org/10.1021/cm970811a

IF: 10.508

1998-01-01

Chemistry of Materials

Abstract:Mesoporous silica spheres ranging from 2 to 6 μm in size were synthesized under static acidic conditions by mixed cationic−nonionic surfactant templating. The mesoporous structure of the calcined silica microspheres was characterized by X-ray diffraction (XRD) and nitrogen sorption, whereas the morphology and size of the microspheres were revealed by scanning electron microscopy (SEM). It was shown that stirring is unfavorable for the formation of silica spheres in the present synthesis. The growth of the micrometer-sized mesoporous silica spheres was examined by transmission electron microscopy (TEM), and an undirectional aggregation process was proposed for the formation of these spheres.
A Facile Route to Synthesis of Hollow SiO2/Al2O3 Spheres with Uniform Mesopores in the Shell Wall

YQ Jiang,XF Ding,JZ Zhao,Hari-Bala,X Zhao,YM Tian,KF Yu,Y Sheng,YP Guo,ZC Wang

DOI: https://doi.org/10.1016/j.matlet.2005.04.037

IF: 3

2005-01-01

Materials Letters

Abstract:The hollow SiO2/Al2O3 spheres with uniform mesopores in the shell wall have been successfully synthesized by a sol–gel process in an oil/water/oil (O/W/O) microemulsion. The intact hollow spheres are obtained by washing the as-synthesized solid produces with boiling water to remove the organic components. A large amount of silanol groups are retained in the hollow spheres by this facile route without calcination, and the possible agglomeration of the spheres and collapse of hollow structures are effectively avoided. The diameter and shell thickness of the spheres are measured by scanning electron microscope (SEM) and transmission polarized light microscope, which are ca. 10 and 2 μm, respectively. TEM image and N2 adsorption–desorption isotherms suggest that uniform mesopores are present in the shell wall of hollow SiO2/Al2O3 spheres after treatment with boiling water. 27Al NMR spectrum indicates almost all of aluminium species of hollow SiO2/Al2O3 spheres are in the four-coordinated environment.
One-step Synthesis of Highly Monodisperse Hybrid Silica Spheres in Aqueous Solution.

Tian-Song Deng,Qi-Feng Zhang,Jun-Yan Zhang,Xin Shen,Kong-Tao Zhu,Jin-Lei Wu

DOI: https://doi.org/10.1016/j.jcis.2008.09.063

IF: 9.9

2009-01-01

Journal of Colloid and Interface Science

Abstract:An effective and reproducible method of preparing highly monodisperse organic-inorganic hybrid silica spheres was studied. One process, one precursor (organosilane) and one solvent (water) were used in our experiments. The size of hybrid silica spheres could be adjusted from 360 to 770 nm with relative standard deviation below 2% by controlling the concentration of the organosilane precursor and the ammonia catalyst. The increasing of the precursor concentration increases the particle size while the catalyst concentration has a reverse effect on the particle size. The concept of homogeneous nucleation and growth processes are introduced to explain the formation mechanism and the effect of reaction conditions. The scanning electron microscopy (SEM) images illustrate the copiousness in quantity and the uniformity in size/shape of the particles that could be routinely accomplished in this synthesis. Fourier transform infrared (FT-IR) and (29)Si nuclear magnetic resonance (NMR) spectra confirm the structure of vinyl hybrid silica spheres, where the vinyl group (-CH=CH(2)) exists and connects to the silicon atom. This method has also been extended to design and prepare other organic-inorganic hybrid materials especially in monodisperse surface-modified silica spheres.
Preparation and Characterization of Monodisperse Nano-silica Spherical

JIANG Huiping,WANG Xiaochuan,ZHONG Fachun,SUN Yi,LIU Yong

2010-01-01

Abstract:The preparation of monodisperse nano-silica spheres by the sol-gel method are described,and the obtained particle size from 480nm to 500nm.The effects of the amount of emulsifier and ammonia water for the nano-size are studied.Nano-particle size,structure and morphology are characterized by laser particle size analyzer(LS),fourier -infrared spectrometer(FI) and scanning electron microscopy(SEM).The consequence demonstrates:The quantity of ammonia water increases,the particle size and the aggregation degree increase;the amount of emulsifier increases, the range of particle size is relatively narrow,but the particle size increases,and also appeares some aggregation.
Systhesis of Monodispersed Silica Microspheres and the Formation Mechanism

LIU Xiumin,WANG Xing,LI Guojie,ZHEN Congmian,GUO Defeng

DOI: https://doi.org/10.13763/j.cnki.jhebnu.nse.2013.03.003

2013-01-01

Abstract:The synthesis conditions of silica microsphere were studied.By adding tetraethoxysilane(TEOS) and ethanol into the catalytic solution uniformly,the monodispersity and spherical degree of the achieved silica microspheres are ideal.When V(TEOS)∶V(NH4OH) is 1∶1,the silica microsphere monodispersity is better and the diameter distribution is narrower.When the reaction temperature is 35 ℃,the generated silica microspheres monodispersity is the best.The suitable synthetized time is 30 min.
Formation Mechanism and Size Control in One-Pot Synthesis of Mercapto-Silica Colloidal Spheres

Zhenda Lu,Lei Sun,Kevin Nguyen,Chuanbo Gao,Yadong Yin

DOI: https://doi.org/10.1021/la1048216

IF: 3.9

2011-01-01

Langmuir

Abstract:Mercapto-silica spheres with controllable size from ∼150 nm to ∼3.5 μm and narrow size distribution have been prepared in water using a one-pot synthesis, in which 3-mercaptopropyltrimethoxysilane (MPS) was used as the sole silica source and ammonia as the base catalyst. The hydrolysis of MPS at the early stage of the reaction produces amphiphilic silicate species which initiate the self-emulsification of the system and lead to the formation of oil-in-water emulsion droplets. Further hydrolysis and condensation promote the nucleation and growth of the mercapto-silica spheres inside the emulsion droplets. These mercapto-silica spheres are both structurally and functionally different from typical silica particles prepared from silicon alkoxides. Understanding the formation mechanism allows systematic tuning of the size of mercapto-silica spheres in a wide range by changing the amount of precursor, the concentration of ammonia, the amount of additional surfactants, and the reaction time. We find that Ostwald ripening may occur quickly if the spheres are kept in the reaction solution, resulting in significant broadening of the particle size distribution. In order to obtain uniform and stable samples, it is important to quench the growth of the mercapto-silica spheres by separating them from the original reaction mixture and then storing them in solvents that can prevent further ripening.
Preparation of Sub-2 Μm Large-Pore Monodispersed Mesoporous Silica Spheres Using Mixed Templates and Application in HPLC

Yajun Du,Lingping Cheng,Long Chen,Yunchao He,Yaling Wu,Shanshan He,Yanxiong Ke

DOI: https://doi.org/10.1016/j.micromeso.2017.02.051

IF: 5.876

2017-01-01

Microporous and Mesoporous Materials

Abstract:Sub-2 mu m large-pore monodispersed mesoporous silica spheres (MMSS) were synthesized by using mixed non-ionic surfactants of dodecylamine (DDA) and dodecylamine polyoxyethylene ether (AC1210) as templates through an alkali-catalyzed silica sol-gel technique combined with the template method. Methanol-H2O volume ratio on morphology was researched in detail. In addition, by using hydrothermal treatment, the average pore size of MMSS could be enlarged to 11 nm from 4.4 nm. The mesoporous silica particles were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), laser particle size analyzer, X-ray diffraction, N-2 physisorption technique. The synthesized sub-2 mu m monodispersed mesoporous silica microspheres were successfully functionalized by dimethyloctadecylchlorosilane and used as a packing material in high performance liquid chromatography (HPLC). (C) 2017 Elsevier Inc. All rights reserved.
Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Huijuan Zhang,Jun Wu,Longping Zhou,Dayong Zhang,Limin Qi

DOI: https://doi.org/10.1021/la062542l

IF: 3.9

2007-01-01

Langmuir

Abstract:Mesoporous silica materials with a variety of morphologies, such as monodisperse microspheres, gigantic hollow structures comprising a thin shell with a hole, and gigantic hollow structures consisting of an outer thin shell and an inner layer composed of many small spheres, have been readily synthesized in mixed water-ethanol solvents at room temperature using cetyltrimethylammonium bromide (CTAB) as the template. The obtained mesoporous silica generally shows a disordered mesostructure with typical average pore sizes ranging from 3.1 to 3.8 nm. The effects of the water-to-ethanol volume ratio (r), the volume content of tetraethyl orthosilicate TEOS (x), and the CTAB concentration in the solution on the final morphology of the mesoporous silica products have been investigated. The growth process of gigantic hollow shells of mesoporous silica through templating emulsion droplets of TEOS in mixed water-ethanol solution has been monitored directly with optical microscopy. Generally, the morphology of mesoporous silica can be regulated from microspheres through gigantic hollow structures composed of small spheres to gigantic hollow structures with a thin shell by increasing the water-to-ethanol volume ratio, increasing the TEOS volume content, or decreasing the CTAB concentration. A plausible mechanism for the morphological regulation of mesoporous silica by adjusting various experimental parameters has been put forward by considering the existing state of the unhydrolyzed and partially hydrolyzed TEOS in the synthesis system.

Synthesis of Nanometer-Sized Mesoporous Oxide Spheres

Synthesis of Nanometer-sized Mesoporous Silica and Alumina Spheres

Synthesis of Mesoporous Silica Spheres by Using Neutral-cationic Surfactant and Semi-batch Growth

Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

One-pot Template-Free Synthesis of Mesoporous Boehmite Core–shell and Hollow Spheres by a Simple Solvothermal Route

Synthesis of Novel Mesoporous Silica Spheres with Starburst Pore Canal Structure

Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Synthesis of monodispersed mesoporous silica spheres (MMSSs) with controlled particle size using gemini surfactant

Preparation of Nano-Sized Mesoporous Silica Dioxide and Al-Doped Silica Dioxide at Extremely Low Reactant Concentration

Synthesis of micrometer-sized hard silica spheres with uniform mesopore size and textural pores

The Size-Controllable Synthesis of Nanometer-Sized Mesoporous Silica in Extremely Dilute Surfactant Solution

Micrometer-Sized Mesoporous Silica Spheres Grown under Static Conditions

A Facile Route to Synthesis of Hollow SiO2/Al2O3 Spheres with Uniform Mesopores in the Shell Wall

One-step Synthesis of Highly Monodisperse Hybrid Silica Spheres in Aqueous Solution.

Preparation and Characterization of Monodisperse Nano-silica Spherical

Systhesis of Monodispersed Silica Microspheres and the Formation Mechanism

Formation Mechanism and Size Control in One-Pot Synthesis of Mercapto-Silica Colloidal Spheres

Preparation of Sub-2 Μm Large-Pore Monodispersed Mesoporous Silica Spheres Using Mixed Templates and Application in HPLC

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents