Abstract:MgO was directly dispersed onto zeolite NaY by microwave irradiation to form strong basic sites with high water-stability. Such high water-stability of MgO modified zeolite resulted from the especially low solubility of MgO in water, which could be useful for expanding the application of solid strong bases in those catalytic processes involving water in the reactants or products. In the isomerization of cis-2-butene at 273 K, MgO/NaY exhibited a considerable activity that increased as the loading amount was raised. The activity of MgO/NaY was higher than that of KNO3/KL and KF/AIPO4-5, and was in proportional to the total basicity formed on MgO/NaY sample instead of the soluble basicity. Dispersion of MgO on zeolite NaY created catalytic activity for the dehydrogenation of isopropanol, but it suppressed the dehydration reaction owing to the cover and/or neutralization of acid sites. Moreover, if the yield of acetone, formed in the dehydrogenation, was given in the units of mmol per gram MgO per hour, the values of MgO/NaY and MgO/KL sample were obviously higher than that of MgO itself. This enhance in catalytic activity should be attributed to the high dispersion of MgO on zeolite expanding the surface area of MgO. MgO/NaY showed activity similar to MgO in aldolisation of acetone at 333 K, but the selectivity for diacetone alcohol on MgO/NaY was higher than that on MgO. As a comparison, MgO loaded on alumina or silica exhibited a lower activity than MgO. Based on these facts it was clear that dispersion of MgO on zeolite by microwave irradiation could be a novel way to prepare strong basic shape-selective catalysts.

Preparation of Novel Strong Basic Zeolite-Like Catalyst Cao/Nay by Use of Microwave Irradiation

Novel solid strong base derived from zeolite supported CaO*

High Load Rare-earth β Zeolite Prepared by Solid Medium-In-Situ Synthesis Method and Its Catalytic Cracking Performance

Attempts to create new shape-selective solid strong base catalysts

DISPERSION OF MgO ON NaY ZEOLITE AND ITS CATALYTIC BEHAVIOR

An investigation of KF modification to generate strong basic sites on NaY zeolite

Preparation of new porous catalytic material Al2O3-NaY through hydrolysis of aluminum isopropoxide

Adjusting the host–guest interaction to promote KNO3 decomposition and strong basicity generation on zeolite NaY

Preparing ZrO2/NaY zeolite-based materials for catalytic degradation of N-nitrosamines by use of microwave irradiation

Investigation On The Novel Environment Benign Materials: The Solid Strong Bases Pepared By Use Of Microwave Irradiation And Their Application For Sweetening

New Unusually Strong Solid Basic Material Derived from KL Zeolite Impregnated with KNO3

Attempt to Generate Strong Basicity on Silica and Titania

Studies on Synthesis of Silicotungstic Acid Supported on NaY Zeolite Catalysts by Microwave Radiation and Their Degradation Properties for Linear Alkylbenzene Sulfonates

A Novel Way To Prepare Gamma-Al2o3 Supported So42-/Zro2 Solid Superacid Catalysts For N-Butane Isomerization

Dispersion of Potassium Nitrate and the Resulting Strong Basicity on Zirconia

Preparation of new porous materials Al2O3/NaY by microwave radiation

Generating Basic Sites on Zeolite Y by Potassium Species Modification: Effect of Base Precursor

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Sustainable Synthesis of Core-shell Structured ZSM-5@Silicalite-1 Zeolite

Preparing Amphiphilic Acidic Zeolite Via Chemically Coating Alkylamine