Basic Calcined Mg-Al Hydrotalcite Supported Cobaltphthalocyanines Catalysts for Mercaptan Autoxidation

Hai-chao LIU,Xi-yao YANG,Guo-peng RAN,En-ze MIN

DOI: https://doi.org/10.3321/j.issn:1000-8144.2000.10.004

2000-01-01

Abstract:Two catalysts for mercaptan autoxidation have been prepared by supporting cobaltphthalocyanine tetrasodium sulphonate CoPc(SO3Na)4 and an equimolar mixture of cobaltphthalocyanine tetrasodium sulphonate CoPc(SO3Na)4 and cobaltphthalocyanine tetra(trimethylammonium) iodide CoPc[N(CH3)3I]4 on basic mixed Mg-Al oxide (denoted as Mg(Al)O) derived from thermal decomposition of Mg-Al hydrotalcite n(Mg)/ n(Al). The resulting catalysts, which possess Co(II) oxidation sites and Mg(Al)O basic sites, are effective in sweetening jet kerosene, and clean kerosene with a mercaptan level of less than 2 × 10-5 sulfur has been obtained over these two catalysts at 40°C. The latter catalyst containing CoPc(SO3Na)4 and CoPc[N(CH3)3I]4 is much more active and stable than the former one containing only CoPc(SO3Na)4. The Mg(Al)O-supported CoPc (SO3Na)4 deactivated after being operated in the kerosene flow for 324 h, with less than 60% of the mercaptans being converted to disulfides. However, Mg(Al)O-supported CoPc(SO3Na)4 and CoPc[N(CH3)3I]4 catalysts, even after being used for 480 h, were still able to oxidize about 85% of mercaptans in kerosene, and clean products containing less than 1.4 × 10-5 of mercaptan-sulfur were obtained. The catalysts before and after autoxidation of mercaptan were characterized by means of XRD and ESR. It is shown that the deactivation of Mg(Al) - O - supported CoPc(SO3Na)4 catalyst is probably due to the aggregation of CoPc(SO3Na)4 molecules on Mg(Al)O. All these results show that it is a better way to prepare the catalysts using an equal amount of the two oppositely charged water-soluble cobaltphthalocyanines: CoPc(SO3Na)4 and CoPc[N(CH3)3I]4. This prevents to some extent the aggregation of Co(II) centers and the formation of less active peroxocomplex: - Co(III) - O - O - Co (III) -, thus obtaining catalysts with higher activity and stability compared to that using CoPc (SO3Na)4 only.