Research on dispersed states of the bulking and strengthening agents in the rubber matrix

Liqun Zhang,Yiqing Wang,Yizhong Wang,Youping Wu,Huifeng Zhang,Jianyun He

2000-01-01

Abstract:The dispersed states of ZnO, CaCO3, argil, clay, carbon black and carbon white in SBR matrix were characterized by electronic microscope TEM and SEM. To make a comparison with the above, the dispersed states of clay/rubber nanocomposites were studied and compared with that of clay/PMMA nanocomposite. According to TEM and SEM photos, there are several levels of dispersed structure with different dimension. Mechanical intermix of rubber contributes to the further fragmentation of the dispersed particles. The further fragmentation of the dispersed particles depends on the cohesion and structural feature of the dispersed phase. Especially, just direct mechanical intermix can in some degree induce fragmentation of clay particles to form some nanodimension dispersed particles. There, however, is no way to form ideally uniformly dispersed nanocomposite. In most nanocomposites besides nanocomposites prepared by in-situ polymerization, there are some congeries. The more the loading amount of dispersed phase leads to the more amount of congeries. The definition of the dispersed phase depends on the resolution of the instrument. A new definition of nanocomposite, therefore, was put forward. If in certain resolution, the dimension of dispersed particles which was less than 100nm and these particles have more than 80 percent by weight or by volume of all the dispersed phase, this materials is nanocomposite. From the point of this view, the rubber strengthened by either carbon black or carbon white involved in this paper was nanocomposites.