INTERFACE OBSERVATION OF HYDROXYAPATITE/POLY(DL-LACTIDE) COMPOSITES IMPLANTED INTO BONE TISSUE

Qixin Zheng,Xiaodong Guo,Jingyuan Du,Yong Liu,Dapin Quan,Yuhua Yan,Shipu Li
DOI: https://doi.org/10.3969/j.issn.0258-8021.2000.02.017
2000-01-01
Abstract:To evaluate bone-bonding capability and osteostimulatory potential of self-designed absorbable fracture fixation devices made of hydroxyapatite/poly(DL-lactide) (HA/PDLLA) composites, 43 rabbits with a transverse transcondylar osteotomy of distal femur were fixed intramedullary by a HA/PDLLA rod (diameter, 4.5mm; length, 30 ~ 40mm). The follow-up times were 3, 6, 12, 24 and 36 weeks. Histologic, scanning electron microscopic and biomechanical analyses were done. Results: Histologically, considerable new bone formation were present around the implant as early as three weeks. Direct bony contact at the tissue-implant interface were seen at the cancellous spaces of the condylar. Scanning electron microscope analysis showed that generous HA crystals deposited and grew on the surface of the composites 3 ~ 6 weeks postoperatively. New bone formed by active osteoblasts was seen around the implant and HA particles were directly bonded to it. The push-out strengths at the interface were increased gradually. Conclusion: The self-designed HA/PDLLA composites also possessed some bone- bonding capacity and osteostimulatory potential, which enhanced the bioactivity of the composites and was good for fracture healing.
What problem does this paper attempt to address?