Preparation And Formation Mechanism Of Elongated (Ca,Dy)-Alpha-Sialon Powder Via Carbothermal Reduction And Nitridation
Juntong Huang,Heping Zhou,Zhaohui Huang,Guanghua Liu,Minghao Fang,Yan'Gai Liu
DOI: https://doi.org/10.1111/j.1551-2916.2012.05145.x
IF: 4.186
2012-01-01
Journal of the American Ceramic Society
Abstract:(Ca,Dy) co-stabilized a-Sialon with elongated grains was prepared from SiO2-AlN-CaF2-Dy2O3 powders by carbothermal reduction-nitridation (CRN) at 1700 degrees C. Detailed investigations on the formation process of (Ca,Dy)-alpha-Sialon elongated grains performed under various firing conditions revealed that the big quartz particles were initially reduced and decomposed gradually by carbon, and a large number of ball-shaped particles consisting of amorphous (Si,Al,Ca,Dy)x(O,N)y were formed. With increasing temperature, nitrogen continuously diffused nto the liquid to form nitrogen-rich solid balls. Further increasing the temperature to 1700 degrees C and held for 2 h, hollow alpha-Sialon spheres with nanometric particles were obtained from nitrogen-rich solid balls. Subsequently, the framework structure of hollow spheres was destroyed at 1700 degrees C for 3 h, and (Ca,Dy)-alpha-Sialon grains grew up continuously by consuming nanometric particles in the rough interface via Ostwald ripening and growth stages moving on the smooth interface. Finally, (Ca,Dy)-alpha-Sialon developed well-defined crystalline elongated grains because the growth rate of rough surfaces is more rapid than that of smooth surfaces.