Undercooling heredity of Cu70Ni30 melt solidified in non-catalytic nucleation coated mould

Xuefeng Guo,Yongchang Liu,Gencang Yang,Jiandong Xing
IF: 3.752
2000-01-01
Transactions of Nonferrous Metals Society of China
Abstract:A new concept of undercooling heredity is developed to evaluate the undercooling ability in a non-catalytic nucleation coated mould, where alloy melts were highly undercooled previously. Before the heredity experiment a noncatalytic nucleation composite glass-lined coating (B-F) was prepared on the inner surface of mould and the Cu70Ni30 alloy was selected to perform undercooling experiment in the BF non-catalytic coating mould. Its ratio of undercooling heredity was 0.76. The results prove that the B-F coating is an ideal non-catalytic media for purified Cu70Ni30 alloy melts due to its small contact angle between the melt and coating layer. Considering that various microstructures form under different undercoolings, two critical undercoolings, Delta T-1 and Delta T-2, and their corresponding microstructures of Cu70Ni30 alloy are well defined. Moreover, it is found that the manned-trigging solidification in the non-catalytic coating mould could be used to get directional undercooling dendrite structure while the melt undercooling is larger than the critical undercooling Delta T-2.
What problem does this paper attempt to address?