Abstract:In recent years, Mg-Zn-Y-Zr alloys have attracted significant interest due to the high strength at room and elevated temperature. Current researches mainly focus on the microstructures and mechanical properties of Mg-Zn-Y-Zr alloys, however, the corrosion behaviors of Mg-Zn-Y-Zr alloys have been seldom studied. In the present paper, the mass loss corrosion and electrochemical corrosion behavior of three Mg-Zn-Y-Zr alloys with Zn contents of 4.3% (mass fraction), 6% and 8.6% in 5% (mass fraction) NaCl solution were studied, respectively. The morphology, microstructure and phase composition of these alloys after different immersion time were observed. The results showed that the type of second phase and the content of Zn in these alloys significantly affect their corrosion resistance performance and the Mg-Zn-Y-Zr alloy with 4.3% Zn exhibited better corrosion resistance. With the increase of Zn content, the W phase with stronger effect of galvanic corrosion formed at grain boundaries and the content of Zn in alpha-Mg matrix also increased, which resulted in the worse corrosion performance Experimental results also showed that the corrosion process of Mg-4.3Zn-0.7Y-0.6Zr alloy can be divided into three stages: galvanic corrosion, Zr-rich zone-Zr-poor zone corrosion and pitting corrosion.

Analysis of transient current for LY12CZ aluminum alloy in NaCl solution during corrosion fatigue

INFLUENCES OF STRESS AMPLITUDE ON THE TRANSIENT CURRENT BEHAVIOR FOR LY12CZ ALUMINUM ALLOY DURING CORROSION FATIGUE

Investigation on corrosion fatigue properties of TA15 alloy in 3.5%NaCl salt spray

STUDY OF CORROSION FATIGUE FOR LY12CZ ALUMINUM ALLOY RIVETED LAP-SPLICE JOINTS

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Transient Current Behaviour for Iron in 3.5%nacl and 3.5%nacl+1%nano2 Solutions During Corrosion Fatigue

Study on the Corrosion Behavior and Mechanism of 6061 Aluminum Alloy under Alternating Current Interference in 3.5% NaCl Solution

Corrosion Behaviour of Ly12 Alloy under Thin Electrolyte Films

Corrosion of Ly12 Aluminum Alloy in Sodium Chloride Solution

Corrosion Fatigue Behavior of Fastening Hole Structure and Virtual Crack Propagation Tests

Electrochemical noises of LC4, LY12 and pure Al in NaCl solution

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Corrosion behavior of magnesium and its alloy in NaCl solution

Shot Noise Analysis on Corrosion Behavior of Zinc Alloy (znal4cu1) under Dry-Wet Cycles

Corrosion Morphology for LY12 Aluminum Alloy Friction Stir Welded in 3.5% NaCl Solution

Electrochemical noise features of pure aluminum during pitting corrosion in neutral NaCl solution

Corrosion evaluation of Al-Cu-Mn-Zr cast alloys in 3.5% NaCl solution

Corrosion Behavior of Pure Zinc and Its Alloy under Thin Electrolyte Layer

Electrochemical features during pitting corrosion of LY12 aluminum alloy in different neutral solutions

Corrosion and passive behavior of AlxCrFeNi3−x (x = 0.6, 0.8, 1.0) eutectic high entropy alloys in chloride environment

Investigation of Az91d Magnesium Alloy Corrosion Behavior under Thin Electrolyte Layer Using Nondestructive Electrochemical Techniques