Modifying NaY Zeolite with Metal Oxide by Microwave Irradiation:Influence on the Adsorption and Decomposition of N-nitrosamines

LL Ma,B Shen,JH Zhu,JR Xia,QH Xu

2000-01-01

Abstract:Coating MgO.br ZrO2 on zeolite NaY accelerated decomposition of N-nitrosodimethylamine and N-nitrosopyrrolidine, resulting from variation of the surface state such as generation of basic sites.

What problem does this paper attempt to address?

Preparing ZrO2/NaY zeolite-based materials for catalytic degradation of N-nitrosamines by use of microwave irradiation

JiaRong Xia,Jianhua Zhu,Yuan Chun,Ying Wang,RuiKang Jia

2001-01-01

Acta Chimica Sinica

Abstract:Zirconia can be coated on zeolite NaY to modify the surface acid-basic properties of the zeolite and to form novel porous materials with framework of the zeolite by microwave radiation. The dispersion threshold of ZrO2 on zeolite NaY is found to be about 10%. On this new material ZrO2/NaY, N-nitrosopyrrolidine (NPYR) is easier to degrade than on either parent zeolite or zirconia. When this degradation process occurrs in air, the formation of NOx can be dramatically suppressed. It is favorable to protect environment and public health.
Microwave‐induced Degradation of Nitrosamines Trapped in Zeolites

Ja Hui Xu,Yu Zhou,Jing Jia Wen,Zheng Ying Wu,Chun Fang Zhou,Jian Hua Zhu

DOI: https://doi.org/10.1002/apj.176

2008-01-01

Asia-Pacific Journal of Chemical Engineering

Abstract:A new method is reported for the degradation of nitrosamines trapped by zeolites. Significant amount of N-nitrosodiphenylamine (NDPA) ill dichloromethane Solution, Lip to one-third, could be degraded by microwave within 1 min once they were adsorbed by zeolite. The nitrosamine molecule, resulting from the electrostatic interaction between the N-NO group of NDPA and the cation of zeolite. could be partially anchored inside the channel of zeolite depending on the degree of structure matching between the adsorbent and the adsorbate. Anchoring of nitrosamines limited their movement so that they were degraded by microwave irradiation. Mesoporous SBA-15 and amorphous silica in Solution Could also promote the microwave-induced degradation of NDPA, owing to the interaction between the Surface Si-OH and the N-NO group of NDPA, and introducing copper oxide increased the conversion of NDPA. In addition. the influence of pore structure of zeolite on the microwave-induced degradation of volatile nitrosamines was examined and discussed. and NaA exhibits a stronger adsorption than NaY for N-nitrosopyrrolidine (NPYR). (C) 2008 Curtin University of Technology and John Wiley & Sons, Ltd.
30-P-08-zro2/nay: A New Material for Removal of N-nitrosamines Pollution

J.H. Zhu,J.R. Xia,Ying Wang,G. Xie,J. Xue,Y. Chun

DOI: https://doi.org/10.1016/s0167-2991(01)81729-8

2001-01-01

Abstract:This chapter presents zirconium dioxide (ZrO2)/NaY, a novel material for the removal of N-nitrosamines pollution. Zirconia can be coated in NaY by microwave radiation and the content of ZrO2 is about 10 wt%. Loading ZrO2 generate some basic sites on the surface of zeolite NaY so that more N-nitrosopyrrolidine (NPYR) can be degraded at lower temperature than that on the parent zeolite. When the carrier gas in the degradation reaction is changed from nitrogen to air, the maximum concentration of NOx formed on ZrO2/NaY is dramatically decreased below 10 μmol/g though most of the N-nitrosamines confirm to be degraded instead adsorbed on ZrO2/NaY. Nitrogen is formed in degradation of NPYR as the main product over the ZrO2/NaY composite, resulting from the special catalytic function of dispersed ZrO2. With high activity for decomposition of N-nitrosamines and suppression for formation of NOx, ZrO2/NaY can be a functional material for removing N-nitrosamines pollution from environment.
Influence of Alkali Treatment on Structure and Catalytic Performance of ZSM-5 Films

YUAN Fang,LI Gang,HU Shenlin

DOI: https://doi.org/10.3969/j.issn.1001-8719.2014.01.022

2014-01-01

Abstract:ZSM-5 films were prepared on the surface of stainless steel plates or tubes by means of in-situ growth method. The influence of alkali treatment on structure and catalytic performance of ZSM-5 films were studied. The results showed that the treatment of ZSM-5 films in 0.2 mol/L NaOH solution with long time or high temperature caused formation of cracks in the film, which could affect the adhesion strength between the film and the substrate. Under appropriate conditions of alkali treatment, the formation of cracks in the film could be avoided. The mesopores could not be produced in the film under the conditions at which mesopores could be formed in the powdery sample. The amorphous materials presented on the film surface were dissolved during alkali treatment, thus the catalytic performance of the film would be improved.
Investigation on Catalytic Decomposition of N-Nitrosamines over Zeolites

J Xue,JH Zhu,B Shen,LL Ma

DOI: https://doi.org/10.3866/pku.whxb20010806

2001-01-01

Abstract:Decomposition of N-nitrosodimethylamine (NDMA) and N-nitrosopyrrolidine (NPYR) on zeolite Y and ZSM-5 was investigated by means of temperature programmed surface reaction(TPSR) combined with GC-MSD and IR techniques. Degradation of N-nitrosamine strongly depended on the activity of zeolite and was accelerated by acid sites. Products of N-nitrosamines degradation were changed by zeolite catalysis, cyano derivative appeared as the main product on NaZSM-5 and NaY zeolites similar to that in pyrolysis while dimethylamine became the dominant one on HZSM-5 and HY. Different reactions are thus proposed: on the latter the Bronsted acid sites probably play the role of main catalytic sites, hence N-nitrosamines degrades to amines while on the former N-nitrosamines may decompose through radical reaction process, similar to the process of pyrolysis. Protonation of zeolite NaY or NaZSM-5 is proved not to be necessary for decomposition of N-nitrosamines. Zeolites are proved to be the novel materials for removing N-nitrosamines pollutants from environment.
Decomposition of N-Nitrosamines over Zeolites

B Shen,LL Ma,JH Zhu,QH Xu

DOI: https://doi.org/10.1246/cl.2000.380

2000-01-01

Chemistry Letters

Abstract:The strong adsorption of zeolite Y and ZSM-5 for N-nitrosamine such as N-nitrosodimethylamine and N-nitrosopyrrolidine was firstly revealed by use of adsorption, temperature programmed surface reaction and TG-DTA techniques. Zeolite can adsorb N-nitrosamines without interference of organic solvent, which will be helpful for removal of the N-nitrosamines pollution in environmental protection.
Microwave-induced Degradation of N-nitrosodimethylamine (NDMA) Sorbed in Zeolites: Effect of Mineral Surface Chemistry and Non-Thermal Effect of Microwave

Yuanan Hu,Yuanzhen He,Hefa Cheng

DOI: https://doi.org/10.1016/j.jclepro.2017.11.014

IF: 11.1

2018-01-01

Journal of Cleaner Production

Abstract:N-nitrosodimethylamine (NDMA), a highly toxic and carcinogenic disinfection byproduct, cannot be efficiently removed by conventional water treatment processes, while sorption by microporous minerals, followed by destruction with microwave irradiation has been developed as a promising alternative. This work examined the impact of surface cation density and type on sorption of NDMA on dealuminated ZSM-5 zeolites, and on microwave-induced degradation of the sorbed NDMA, as well as the non-thermal effect of microwave. NDMA sorption was found to increase with the framework Si/Al ratio of dealuminated ZSM-5 zeolites (i.e., decreasing density of surface cations), and was also influenced by the type of surface cations. Degradation of the sorbed NDMA proceeded faster with increases in the power level of microwave and in the micropores with higher densities of surface cations, which was attributed to the increases in the number and/or temperature of micro-scale "hot spots" formed by microwave dielectric superheating of the surface cations. The degradation rate of sorbed NDMA was also found to be inversely correlated with the hydration free energy of surface cations present in the zeolite micropores. The apparent activation energy estimated from the temperature dependence of NDMA degradation in the micropores under microwave irradiation was 18.2 kJ/mol, which is much lower than those of typical thermolysis reactions and is indicative of significant contribution from the non-thermal effect of microwave. (C) 2017 Elsevier Ltd. All rights reserved.
Eliminating Carcinogens in Environment: Degradation of Volatile Nitrosamines by Zeolites Y and ZSM-5

Zheng Ying Wu,Hong Ji Wang,Li,Jun Xue,Jian Hua Zhu

DOI: https://doi.org/10.1016/j.micromeso.2007.05.066

IF: 5.876

2007-01-01

Microporous and Mesoporous Materials

Abstract:To open the new application of zeolite in protection of environment and public health, degradation of volatile nitrosamines in zeolite Y and ZSM-5 is studied to explore the influence of pore structure and cation of zeolite on the reaction, and the impact of reaction conditions, including different carrier gas and pre-adsorbed moisture and amines, on the decomposition of N-nitrosopyrrolidine (NPYR) is also examined. NPYR can be degraded by these zeolites with sodium cation, and the possible degradation path is discussed. Due to the bigger pore size and the larger pore volume, zeolite NaY can adsorb and degrade more NPYR than NaZSM-5 and in general the acidic zeolite exhibits a higher activity than its basic analogue to decompose nitrosamines.
Adsorption and Decomposition of N-nitrosamines on Zeolites

马丽丽,严冬,朱建华

DOI: https://doi.org/10.3969/j.issn.0253-2328.2001.02.048

2001-01-01

Abstract:In this short paper,adsorption and catalytic decomposition of N-nitrosamines such as NDMA and NPYR on NaY,HY,HZSM-5 and NaZSM-5 zeolites were investigated by use of GC-MSD,TPSR techniques,and the products distribution were also analyzed.Of zeolite catalysis dramatically lowers the temperature needed for the degradation of N-nitrosamines.Degradation of NDMA on NaZSM-5 or NaY zeolites produced mainly cyano derivative same as that of pyrolysis,while on HZSM-5 or HY dimethylamine became the dominant product as the GC-MS spectra demonstrated.Consequently different reactions are proposed to occur on the zeolites with proton or sodium ions.On the former the Bronsted acid sites probably play the role of main catalytic sites,hence N-nitrosamines degrades to amines while on the latter N-nitrosamines decomposed through radical reaction process,similar as pyrolysis. Zeolite can selectively adsorb N-nitrosamines from solution,but degradation of NDMA or NPYR on zeolite kept to high temperature,indicating the strong adsorption of NPYR on zeolite ZSM-5 which means no N-nitrosamines can desorb from the adsorbent at ambient temperature. Unlike pyrolysis by which the conversion of NPYR was only 1.3% at 593?K while NDMA did not react noticeable,NPYR began to decompose at 523?K on zeolite NaY and NDMA at 593?K.Degradation of N-nitrosamines strongly depends on the pore structure of zeolite, and the acid sites of zeolite accelerate degradation of N-nitrosamines,so that NDMA began to decompose at 513?K on HZSM-5 zeolite but at 553?K on NaZSM-5.However,activation of zeolite NaY at 773?K seems to have almost no influence on TPSR of NPYR,since similar TPSR spectrum was found of both activated and non-activated samples;so that zeolite can be used for removing N-nitrosamines pollution without activation.
30-P-07-degradation of N-nitrosamines on Zeolites

J.H. Zhu,B. Shen,Y. Xu,J. Xue,L.L. Ma,Q.H. Xu

DOI: https://doi.org/10.1016/s0167-2991(01)81728-6

2001-01-01

Abstract:This chapter discusses a degradation of N-nitrosodimethylamine (NDMA) and N-nitrosopyrrolidine (NPYR) on zeolites by use of temperature-programmed surface reaction (TPSR) and gas chromatography–mass spectrometry (GC–MS). Activation of zeolite had almost no effect on TPSR of NPYR, as zeolite could selectively adsorb N-nitrosamines. Cyano derivative appear as the main product on NaZSM-5 or NaY zeolites similar to that in pyrolysis while DNA becomes the dominant one on HZSM-5 or HY. On the latter, the Brönsted acid sites probably play the role of main catalytic sites, hence N-nitrosamines degrades to amines on Brönsted acid sites while on the former N-nitrosamines might decompose through radical reaction process, similar as pyrolysis. No desorption of the N-nitrosamines occurs on zeolites even at elevated temperature and protonation of zeolite.
DISPERSION OF MgO ON NaY ZEOLITE AND ITS CATALYTIC BEHAVIOR

Wang Ying,Chun Yuan,Zhu Jianhua,Zhu Haiyan,Qin Yu,Xu Qinhua

DOI: https://doi.org/10.3321/j.issn:0253-9837.1999.04.009

IF: 16.5

1999-01-01

Chinese Journal of Catalysis

Abstract:MgO was directly dispersed onto zeolite NaY by microwave irradiation to form strong basic sites with high water-stability. Such high water-stability of MgO modified zeolite resulted from the especially low solubility of MgO in water, which could be useful for expanding the application of solid strong bases in those catalytic processes involving water in the reactants or products. In the isomerization of cis-2-butene at 273 K, MgO/NaY exhibited a considerable activity that increased as the loading amount was raised. The activity of MgO/NaY was higher than that of KNO3/KL and KF/AIPO4-5, and was in proportional to the total basicity formed on MgO/NaY sample instead of the soluble basicity. Dispersion of MgO on zeolite NaY created catalytic activity for the dehydrogenation of isopropanol, but it suppressed the dehydration reaction owing to the cover and/or neutralization of acid sites. Moreover, if the yield of acetone, formed in the dehydrogenation, was given in the units of mmol per gram MgO per hour, the values of MgO/NaY and MgO/KL sample were obviously higher than that of MgO itself. This enhance in catalytic activity should be attributed to the high dispersion of MgO on zeolite expanding the surface area of MgO. MgO/NaY showed activity similar to MgO in aldolisation of acetone at 333 K, but the selectivity for diacetone alcohol on MgO/NaY was higher than that on MgO. As a comparison, MgO loaded on alumina or silica exhibited a lower activity than MgO. Based on these facts it was clear that dispersion of MgO on zeolite by microwave irradiation could be a novel way to prepare strong basic shape-selective catalysts.
Microwave Assisted NaOH Modified Zeolite and Its Adsorption Properties of Zn2+

Li Yinhuan,Zhang Xiulan,Jin Ya’ nan,Zhang Wei

DOI: https://doi.org/10.3969/j.issn.1003-0972.2015.01.019

2015-01-01

Abstract:The natural zeolite was modified with NaOH assisted with microwave .On the basis of single factor exper-iments,the optimization methods were as follows:0.5 mol/L of NaOH, 480 W of microwave power , 5 min of radiation time.The adsorption behavior of the modified zeolite to Zn 2+in waste water was investigated .The results showed that the modified zeolite could greatly enhance absorption capability of Zn 2+.Under the optimum conditions , the removal rate of Zn2+(50 mg/L) in water by modified zeolite could be up to 95.68%.According to the adsorption isotherm curves , the adsorption model of Langmuir was better than Freundlich in simulating this adsorption process .The adsorp-tion kinetics of modified zeolite can be well described by pseudo-second-order kinetic equation .
Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

WP Zhang,XW Han,XC Liu,H Lei,XM Liu,XH Bao

DOI: https://doi.org/10.1016/s1387-1811(02)00335-9

IF: 5.876

2002-01-01

Microporous and Mesoporous Materials

Abstract:Variations in the microporous structure and non-framework aluminum (AlNF) distribution of HZSM-5 zeolite with a crystal size less than 100 nm dealuminated by thermal and hydrothermal treatment have been investigated by xenon adsorption and 129Xe NMR spectroscopy. The secondary pores in the nanosized HZSM-5 zeolite are observed directly via 129Xe NMR spectroscopy. As evidenced by 129Xe NMR and XPS, for the calcined microsized HZSM-5, most of the AlNF may deposit on its external surface, a small amount of AlNF may be located in its channels. However, for the calcined nanosized HZSM-5, most of the AlNF may be located in the channels, while a small amount of AlNF may be located on the external surface. After hydrothermal treatment at lower temperature, the distribution of AlNF in dealuminated nanosized HZSM-5 is heterogeneous. It is not only present in the channels and on the external surface as in the case of microsized HZSM-5, but also near the pore entrances at the outer edge of the crystallites. However, at higher steaming temperatures, more AlNF in both the microsized and the nanosized HZSM-5 zeolites will migrate to their external surface.
In Situ Ftir Investigation on the Adsorption of Nitrosamines in Zeolites

ZY Yun,Y Xu,JH Xu,ZY Wu,YU Wei,ZP Zhou,JH Zhu

DOI: https://doi.org/10.1016/j.micromeso.2004.04.012

IF: 5.876

2004-01-01

Microporous and Mesoporous Materials

Abstract:Adsorption of N-nitrosohexamethyleneimine (NHMI) on a series of zeolites with different pore sizes and surface acidity was studied by in situ infrared technique, combined with temperature programmed surface reaction (TPSR). The adsorption manner of bulky NHMI in zeolite KA and NaA with pore sizes smaller than the molecular diameter of adsorbate was explored; also the impact of adsorbent pore structure and temperature on the adsorption of the volatile nitrosamines was examined. In comparison, the ordered mesoporous silica SBA-15 was employed to adsorb NHMI, and the acceleration of selective adsorption of nitrosamines by incorporating copper or zinc was checked and directly confirmed, which would be beneficial for expanding the application of mesoporous materials in environment protection and public health.
Capturing Nitrosamines by Zeolite Mcm-22: Effect of Zeolite Structure and Morphology on Adsorption

Jing Yang,Yu Zhou,Jia Yuan Yang,Wei Gang Lin,Ya Jing Wu,Na Lin,Jun Wang,Jian Hua Zhu

DOI: https://doi.org/10.1021/jp9116497

2010-01-01

Abstract:The activity of zeolite MCM-22 in trapping nitrosamines, a class of well-known carcinogenic environmental pollutants, is reported in this article for the first time. MCM-22 possesses a set of unique porous structures and morphologies, making it possible to trap both volatile nitrosamines and bulky tobacco specific nitrosamines. Liquid adsorption and instantaneous gaseous adsorption methods have been employed to study the impact of morphology on MCM-22's ability in adsorbing nitrosamines in both gaseous and liquid media. As-synthesized MCM-22 was subjected to different treatments to induce morphological changes. SEM revealed a special rose-like appearance. The effects of these morphological modifications on MCM-22's adsorption capacities was studied and compared to NaY and NaZSM-5. The results obtained seem to suggest that enhanced collision probability between adsorbate and adsorbent may have an important role to play for MCM-22. Furthermore, the treatments created mesopores in MCM-22 that enhance mass transport within its hierarchical structure.
Attempt to adsorb N-nitrosamines in solution by use of zeolites

Jian Hua Zhu,Dong Yan,Jia Rong Xai,Li Li Ma,Bin Shen

DOI: https://doi.org/10.1016/S0045-6535(00)00560-9

IF: 8.8

2001-01-01

Chemosphere

Abstract:The strong adsorption of zeolite for N-nitrosamines in solution was first revealed by use of adsorption, and temperature programmed surface reaction (TPSR) techniques. N-nitrosodimethylamine (NDMA) and N-nitrosopyrrolidine (NPYR) as well as N-nitrosohexamethyleneimine (NHMI) can be adsorbed on zeolite Y, ZSM-5 and A in the solution of methylene chloride or water, which will be helpful for removal of the N-nitrosamines pollution in environmental protection. The equilibrium data were fitted to Freundlich-type isotherms, but the adsorption capacity of zeolites mainly depended on their pore size, surface area and acid–basic properties. Molecular size of adsorbate and solute–solvent interaction also strongly affected the adsorption of N-nitrosamines on zeolite in solution. The extraordinary adsorption properties of NaA zeolite for N-nitrosamines in aqueous solution is first reported and discussed.
Tailoring the nano-channel of ZrO 2/SBA-15 mesoporous materials for efficiently trapping and degradation volatile nitrosamines

LiYing Shi,Sheng Chu,Fei Kong,Leilei Luo,Ying Wang,Zhigang Zou

DOI: https://doi.org/10.1016/j.solidstatesciences.2011.08.007

IF: 3.752

2011-01-01

Solid State Sciences

Abstract:This article reports a bifunctionalized mesoporous ZrO2/SBA-15 materials prepared through a simplified one-pot synthesis, in which the aged sample was evaporated with mother solution under the self-adjusted pH condition. The results of low-angle XRD, HRTEM, nitrogen adsorption-desorption, in-situ 1H NMR and NH3-TPD tests confirmed the well-ordered hexagonal structure and large pore size of these composites along with the newly formed acidity and basicity. Temperature programmed surface reaction (TPSR) was employed to assess the catalytic function of ZrO2/SBA-15 composites on the degradation of carcinogenic volatile nitrosamines such as N-nitrosopyrrolidine (NPYR). Due to the special interaction between the N–NO group of nitrosamines and the acidic site of mesoporous composite, NPYR could be efficiently trapped and then catalytic degraded at lower temperature, which enables this functional composite to be a new candidate for environment protection.
PREPARATION AND PROPERTIES OF A NEW KIND OF ACID CATALYST OF ZEOLITE COATING ON METAL-SURFACE

JQ LI,JX DONG,GH LIU

DOI: https://doi.org/10.1016/S0167-2991(08)61841-8

1994-01-01

Abstract:The catalytic material of mordenite coating on metal Cr surface (MOR/Cr) is first synthesized by the vapor phase method and characterized by IR, SEM and microprobe techniques. The experimental results show that the crystals of mordenite grow on metal Cr surface and Cr does not enter the mordenite framework. It seems that Cr does not exert any effect on the position of IR absorption bands of mordenite. In HMOR/Cr sample, there exist Si, Al, Cr and a little Na, and the Cr atom content is 1.02% as determined by the microprobe method. As a catalyst, HMOR/Cr shows good catalytic properties for the reaction of o-xylene isomerization.
Adsorption and Room Temperature Degradation of N-nitrosodiphenylamine on Zeolites

CF Zhou,ZY Yun,Y Xu,YM Wang,J Chen,JH Zhu

DOI: https://doi.org/10.1039/b401004c

IF: 3.3

2004-01-01

New Journal of Chemistry

Abstract:N-Nitrosodiphenylamine (NDPA) is selected as a model compound to reveal the specific adsorption and catalytic function of zeolites in the removal of carcinogenic nitrosamines from the environment. The bulky NDPA molecule is indeed adsorbed in the zeolite KA having a small aperture, by insertion of the –N–NO group into the channel and involving a specific interaction between the nitrosamine and the zeolite. Degradation of NDPA at room temperature on zeolite is reported for the first time, revealing the potential applicability of zeolites to eliminate nitrosamines under mild conditions. The acidity of zeolite is the key factor determining its ability to degrade NDPA and, among the zeolites evaluated, Hβ is the most effective catalyst with an activity much higher than that of other zeolites at ambient temperature.
Capturing Nitrosamines by Zeolite A: Molecular Recognition in Subnanometer Space

J. Yang,Y. Zhou,H. J. Wang,T. T. Zhuang,Y. Cao,Z. Y. Yun,Q. Yu,J. H. Zhu

DOI: https://doi.org/10.1021/jp7119729

2008-01-01

Abstract:The adsorption and catalytic degradation of nitrosamines by zeolite A with cesium, potassium, sodium, or calcium cation was systemically studied in the research reported in this article. The results of instantaneous adsorption, temperature-programmed surface reaction, and in situ Fourier transform infrared spectroscopy measurements proved the adsorption of the bulky nitrosamines, N-nitrosonornicotine (NNN) and N-nitrosopyrrolidine, on the zeolite A with a pore diameter of only 0.2-0.5 nm. Moreover, thermogravimetricmass spectrometry analysis revealed the different adsorption and degradation manners of NNN on various samples of zeolite A, which will be discussed in terms of electrostatic attraction and geometric confinement provided by the zeolite.

Modifying NaY Zeolite with Metal Oxide by Microwave Irradiation:Influence on the Adsorption and Decomposition of N-nitrosamines

Preparing ZrO2/NaY zeolite-based materials for catalytic degradation of N-nitrosamines by use of microwave irradiation

Microwave‐induced Degradation of Nitrosamines Trapped in Zeolites

30-P-08-zro2/nay: A New Material for Removal of N-nitrosamines Pollution

Influence of Alkali Treatment on Structure and Catalytic Performance of ZSM-5 Films

Investigation on Catalytic Decomposition of N-Nitrosamines over Zeolites

Decomposition of N-Nitrosamines over Zeolites

Microwave-induced Degradation of N-nitrosodimethylamine (NDMA) Sorbed in Zeolites: Effect of Mineral Surface Chemistry and Non-Thermal Effect of Microwave

Eliminating Carcinogens in Environment: Degradation of Volatile Nitrosamines by Zeolites Y and ZSM-5

Adsorption and Decomposition of N-nitrosamines on Zeolites

30-P-07-degradation of N-nitrosamines on Zeolites

DISPERSION OF MgO ON NaY ZEOLITE AND ITS CATALYTIC BEHAVIOR

Microwave Assisted NaOH Modified Zeolite and Its Adsorption Properties of Zn2+

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

In Situ Ftir Investigation on the Adsorption of Nitrosamines in Zeolites

Capturing Nitrosamines by Zeolite Mcm-22: Effect of Zeolite Structure and Morphology on Adsorption

Attempt to adsorb N-nitrosamines in solution by use of zeolites

Tailoring the nano-channel of ZrO 2/SBA-15 mesoporous materials for efficiently trapping and degradation volatile nitrosamines

PREPARATION AND PROPERTIES OF A NEW KIND OF ACID CATALYST OF ZEOLITE COATING ON METAL-SURFACE

Adsorption and Room Temperature Degradation of N-nitrosodiphenylamine on Zeolites

Capturing Nitrosamines by Zeolite A: Molecular Recognition in Subnanometer Space