Anisotropy and Faraday Effect in Co Spinel Ferrite Films
HY ZHANG,BX GU,HR ZHAI,M LU,YZ MIAO,SY ZHANG,HB HUANG
DOI: https://doi.org/10.1063/1.356741
IF: 2.877
1994-01-01
Journal of Applied Physics
Abstract:Crystalline Co spinel ferrite films were prepared by rf sputtering on glass substrates without buffer layer and annealed at temperatures from 400 to 600 °C for 2 h in air. (100) texture was obtained in these films. The anisotropy constant, magnetic hysteresis loops, and magneto-optical Faraday spectra of the films were measured. The texture became poor when the films were annealed below 500 °C, but the perpendicular anisotropy constant Ku, squareness ratio R=(Mr/Ms)⊥/(Mr/Ms)∥ increased and showed peak values of 2.2×105 ergs/cm3 and 0.94, respectively, at an annealing temperature Ta=500 °C. For the film annealed at 600 °C (higher than the Curie temperature, 520 °C, of Co spinel ferrite), the texture recovered, but Ku and R dropped. The Faraday rotation spectra of Co spinel ferrite films showed a broad peak centered around 720 nm. The peak value increased monotonically with increasing annealing temperature. These results may be related to the Co ion-induced anisotropy and Co ion distribution in tetrahedral sites and octahedral sites.