Abstract:Nanocrystalline titania as photocatalyst has attracted considerable attention for its potential use in environmental cleaning. Recently, lanthanide ions doped titania samples have been shown to increase the photocatalytic efficiency of selected reactions. In this work, TiO2 nanoparticles doped with Er3+ were prepared via an ultrasonic assisted sol-gel method. The optical properties of the samples were determined by photoacoustic (PA) spectroscopy. It was found that the absorption edge shifted to lower wavelength when the particle size fell into nanometer range, which is the evidence of a quantum size effect. The nature of ligand bonding to Er3+ and the structural properties were investigated with the PA absorptions of the f-f transitions of Er3+, which are sensitive to the local environment. The results showed that TiO2 gel heated at 70 °C still contained abundant trapped water and ethanol, and the environment around Er3+ was similar to the one in the aqueous ion. The “degree of covalency” for Er3+ bonding increased continuously during the gel-to-anatase transition. For the sample calcined at 1100 °C, however, the f-f transitions of Er3+ showed blue shifts and the intensity of the hypersensitive transition decreased, indicating an increase of ionicity in the Er3+ bonding. This can be attributed to the segregation of Er3+ ions to the external surface, forming Er2Ti2O7 during the anatase-to-rutile transition, which was confirmed with XRD and TEM measurements.

Photoacoustic spectra studies of nanometer BaTiO3

PHOTOACOUSTIC SPECTRA STUDIES OF NANOMETER SrTiO3

Optical Absorptions of Nanoscaled Cotio3 and Nitio3

Study of Erbium (iii) Doped Titanium Dioxide Nanoparticles by Photoacoustic Spectroscopy

A study on the local environment of lanthanide ion in nanocrystalline titania

Temperature Effect on the Structure and Optical Properties of Eu/TiO2 Nanomaterials

Lanthanide absorption spectral probe in titania nanoparticles synthesized by ultrasonic assistant solgel method

Photoacoustic Study on the Structural Variation of Titania Nanomaterials Using the Pr (iii) Ion As A Spectral Probe

Photoacoustic Study of \mathrm{Y}^{3+}-, \mathrm{Tb}^{3+}- , and \mathrm{Er}^{3+}-Doped Zinc Oxide Nanocrystals

Identification of local phase of nanoscale BaTiO₃ powders by high-resolution electron energy loss spectroscopy.

Microwave absorption enhancement and electron microscopy characterization of BaTiO₃ nano-torus.

Study on the Phase Transition of Lanthanide-Doped Titania Nanoparticles by Photoacoustic Spectroscopy

Photoacoustic Study of $$\mathrm{Y}^{3+}$$-, $$\mathrm{Tb}^{3+}$$Tb3+- , and $$\mathrm{Er}^{3+}$$Er3+-Doped Zinc Oxide Nanocrystals

Phonon Properties and Microstructure of Annealed Litao3:Nd

Pressure-Induced Phase Transition in BaTiO 3 Nanocrystals

Study of Structural and Photoluminescent Properties in Barium Titanate Nanocrystals Synthesized by Hydrothermal Process

Photoacoustic Study of Y^3+ -, Tb^3+ - , and Er^3+ -Doped Zinc Oxide Nanocrystals

Temperature Evolution of the Fano Line Shape in the Raman Spectra of BaTiO3 Nanoparticles

Study of Enhanced Photoabsorption of Bao Thin Films in the Near-Ultraviolet Band with Applied Vertical Electric Field on the Surface

Effect of Oxygen Partial Pressure and Anneal Temperature on Batio3 Thin Film Crystal Structure

Photoacoustic Study of $$\mathrm{Y}^{3+}$$ Y 3 + -, $$\mathrm{Tb}^{3+}$$ Tb 3 + - , and $$\mathrm{Er}^{3+}$$ Er 3 + -Doped Zinc Oxide Nanocrystals