Abstract:Rod-like and spheric mercury sulfide (HgS) microcrystallites with hexagonal and cubic structure have been synthesized at room temperature by treating HgO with sulfur in ethylenediamine (en). Real time monitoring of both the UV–vis absorption spectrum and Raman spectrum during the dissolution process of sulfur in en solvent have been exploited for the first time to explore the underlying reaction mechanism. The characteristic peaks in absorption and Raman lines originated from the polysulfide ions S62− and S3− are observed in the sulfur–en solution, which are found to decrease in concentration and lifetime with dissolution time, and become undetectable finally. The structure and morphology of the synthesized HgS microcrystallites change with the lifetime of the S6− and S3− ions in the solution. It is further observed that S62− and S3− ions are responsible for the formation of hexagonal structure and spheric-shape morphology, while the en solvent is beneficial to the formation of rod-like single-crystalline HgS.

Room-temperature conversion route to nanocrystalline mercury chalcogenides HgE (E=S,Se,Te)

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

An Oxide Direct Conversion Route to Nanocrystalline Mercury Chalcogenides

Room-Temperature Synthesis of Copper and Silver, Nanocrystalline Chalcogenides in Mixed Solvents

Wet Synthesis and Characterization of Mse (M = Cd, Hg) Nanocrystallites at Room Temperature

Room Temperature Synthesis of Metal Chalcogenides in Ethylenediamine.

A γ-irradiation reduction route to nanocrystalline CdE (E=Se, Te) at room temperature

Sonochemical synthesis of nanocrystalline lead chalcogenides: PbE (E = S, Se, Te)

Synthesis of cadmium chalcogenide nanotubes at room temperature

Hydrothermal synthesis of PbSe, PbTe semiconductor nanocrystals

A solvothermal synthetic route to CdE (E = S, Se) semiconductor nanocrystalline

A Simple, Convenient, Mild Hydrothermal Route to Nanocrystalline CuSe and Ag2Se

A Novel Room Temperature Method to Nanocrystalline Ag2se

Sonochemical Preparation of HgSe Nanoparticles by Using Different Reductants

The synthesis of HgS microcrystallites with controllable structure and morphology

Synthesis and Characterization of Ternary Chalcogenides Ag8SnE6 (E=S, Se)

A room temperature chemical route to nanocrystalline PbS semiconductor

A Simple Method to Synthesize Pbe (E = S, Se) Nanocrystals

A Synthetic Method for Transition-Metal Chalcogenide Nanocrystals.

Solvothermal Route to Nanocrystalline CdSe

A direct solvothermal route to nanocrystalline selenides at low temperature