The Structure and Magnetism of Orthochromites Ho1−xYxCrO3
Hongliang Wang,Xinzhi Liu,Lijie Han,Xiaobai Ma,Wenze Han,Kai Sun,Dongfeng Chen,Hao Guo,Zhendong Fu,Chin-Wei Wang,Pinwen Zhu,Yuntao Liu
DOI: https://doi.org/10.1016/j.jmmm.2018.10.086
IF: 3.097
2019-01-01
Journal of Magnetism and Magnetic Materials
Abstract:The crystal structure, dynamics, magnetic structure and property of orthochromites solid solution Ho1-xYxCrO3 (x = 0, 0.2, ..., 1.0) were systematically investigated by X-ray diffraction, Raman scattering, magnetometry and neutron powder diffraction. With increasing non-magnetic Y3+-substitution for Ho3+ throughout the whole range, the crystallographic parameters remain almost unchanged, so is Ned temperature (T-N approximate to 141 K), which is closely related to the structure in these orthochromites. However, the Raman spectra demonstrates the lattice dynamics is influenced due to the mass difference between Ho3+ and Y3+. Moreover, the spin reorientation property is also strongly affected by Y-substitution revealed by neutron powder diffraction. For the composition of x <= 0.6, the magnetism of Cr3+ sublattice adopts Gamma(2) spin configuration in terms of Bertaut notation from low temperature (10 K) up to Neel temperature. With the doping concentration further increases to x = 0.7 and 0.8, the system exhibits a mixed structure of (Gamma(2) + Gamma(4) ) within a certain temperature range. Beyond and underneath of which, a single spin configuration is identified as Gamma(4) (G(x)A(y)F(z) ) and Gamma(2) (F(x)C(y)G(z)), respectively. After x = 0.8, only Gamma(4) (G(x)A(y)F(z) ) are observed below T-N. These phenomena are attributed to the weakened Ho3+-Cr3+ interaction with Y-substitution, which causes a competition between Gamma(2) and Gamma(4) spin configurations.