Seeded Emulsion Polymerization of Methyl Acrylate Onto Polyvinyl Acetate Initiated by 2,2-Azobisisobutyronitrile

CY Kan,MH Liu,Q Yuan,MQ Hong,XZ Kong

DOI: https://doi.org/10.3969/j.issn.1671-9352.1999.02.013

1999-01-01

Acta Polymerica Sinica

Abstract:Seed latex particles of polyvinyl acetate(PVAc) with narrow diameter distribution were first prepared by using ammonium persulfate as initiator, then unswelling and swelling seeded emulsion polymerization of methyl acrylate(MA) onto PVAc initiated by 2, 2'-azobisisobutyronitrile(AIBN) were carried out at 60 degrees C in the absence of emulsifier. In order to investigate particle morphologies of various seeded latexes, a selective staining technique using phosphotungstic acid(PTA) was used under transmission electron microscopy(TEM) observation. Results showed that experimental particle size agree roughly with calculated particle size for all of seeded emulsion polymerizations, but particle morphologies are different. Under unswelling condition, taking into account the high water solubility of MA, its homonucleation in water was significant, and PMA secondary particles were formed and coagulated onto the PVAc particles, so initiation and polymerization loci of MA were both in PVAc seed particle and in water phase, and PMA domains were observed at the surface and inside of seeded latex particles when PVAc/MA weight ratios are 2 and 1. When PVAc/MA weight ratio decrease to 0.5, PMA-PVAc core-shell particle was observed. While under swelling condition, the inner of PVAc particle swelled with MA was main loci of initiation and polymerization of MA, no PMA domains or core-shell structure were observed, and interpenetrating network structures were formed for different PVAc/MA ratios.