Abstract:Through a typical solid-state reaction followed by planetary ball milling, ABO 3 structured perovskite Bi 0.5 Na 0.5 ZrO 3 (BNZ) was employed as an additive to create the lead-free piezoceramic composite having compositional formula K 0.47 Na 0.47 Li 0.06 NbO 3 +(x)Bi 0.5 Na 0.5 ZrO 3 where x = 0.0 wt% to 0.5 wt%. The prepared composites were characterized with the help of XRD, SEM, and FTIR. The XRD results indicated manifestation of morphotropic phase boundary (MPB), i.e. orthorhombic-tetragonal (O-T) phase boundary, for 0.4 wt% and 0.5 wt%. The SEM pictures revealed the microstructural properties of grain-grain size distribution and the average grain size of the composites. The elemental composition examination using EDAX revealed no foreign element contamination. The FTIR examination verified the development of perovskite, indicating that the BNZ has correctly fused into the KNLN matrix. The DC resistivity (ρdc) behavior was determined from IV and IR curves measured at room temperature together with varied temperature line up from 30 °C to 150 °C and a high dc resistivity ρ dc of order ≈ 10 9 Ω cm was obtained for all the ceramics. The results have been analyzed and the mechanism pertaining to the results has been discussed in the paper. Thus the main idea was to develop a lead-free piezoceramic composite by incorporating Bi 0.5 Na 0.5 ZrO 3 as an additive and investigating its effect on the above mentioned properties of the composite material.

THE SYNTHESIS OF A NEW NIOBATE COMPOUND K6Zr2Nb14O42

ChemInform Abstract: Synthesis, Structures, Optical Properties and Electronic Structures of Two Mixed Metal Borates MBaB5O9 (M: Na, K).

Synthesis of complex niobate nanostructures via molten-salt reaction: Effect of ZrO 2 on product morphology

Synthesis, Optical and Electrical Properties of High-Entropy Niobate (Mg0.2Cu0.2Ni0.2Co0.2Zn0.2)Nb2O6 with a Columbite Structure

Structural Stability, Electronic Structure, and Superconductivity of Cubic Sodium Hexaboride NaB6 from First-Principle Calculations

Synthesis of CaNb2O6 with a Rynersonite-like Structure: Morphology, Rietveld Refinement, Optical, and Vibrational Properties

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Hydrothermal Synthesis and Structure of K3Na5(H2NCH2CH2NH3)2{(VO)12O6[B3O6(OH)]6}(H2O)·12H2O

Synthesis, Structure Characterization and Fluorescence Property of a New Fluoride Borate Crystal, CdZn2KB2O6F.

Synthesis and Characterization of Nanocrystalline Niobates

Synthesis and characterization of a new rare earth borate nonlinear optical crystal K 7 PbLu 2 B 15 O 30

Synthesis and Large Cell Structure of Eu2Cu2/3Nb4/3O7

Crystal structure characteristics, dielecric properties and vibrational spectra of Nb-rich non-stoichiometric Ba[(Zn1/3Nb2/3)1−xNbx]O3 ceramics

Synthesis, Crystal Structure, Characterization and Luminescent Properties of Kbatbb2o6

Preparation, Structural and Optical Properties of a New Class of Compounds, Bi2MNbO7 (m=al, Ga, In)

Crystal Structure, Ferroelectricity and Polar Order in a Ba4R2Zr4Nb6O30 (R = La, Nd, Sm) Tetragonal Tungsten Bronze New System

Synthesis, characterization, and theoretical analysis of three new nonlinear optical materials K7MRE2B15O30 (M= Ca and Ba, RE= La and Bi)

Syntheses, structures and characterization of noncentrosymmetric MZnPO 4 (M = K, NH 4 )

A Novel Mixed-Metal Borate with Large [B12O18(OH)6]6- Motif: Synthesis, Structure and Property

Structural, Electrical Studies of K0.47Na0.47Li0.06NbO3+(x) Bi0.5Na0.5ZrO3 Composites