ELLIPSOMETRIC STUDIES OF ALBUMIN AND FIBRINOGEN ADSORPTION ON SILICA AND POLYURETHANE FILM SURFACES

Yong Hu,Xuemei Zeng,Yandao Gong,Senfang Sui,Nanming Zhao

DOI: https://doi.org/10.3969/j.issn.0258-8021.1998.01.009

1998-01-01

Abstract:Adsorption behavior of bovine serum albumin(BSA) and human fibrinogen(FGN) was studies using ellipsometry. It is shown that the final amount of adsorbed BSA is less than that of FGN at equal protein concentration when the concentration is above 5μg/ml. With changed protein concentration, the adsorption of BSA showed to be saturated at concentration of 10μg/ml(namely, the final amount of adsorbed protein does not increase further with the increase of the protein concentration) while the concentration for FGN adsorption saturation is 20μg/ml. At equal protein concentration of 30μg/ml, both the adsorption speed and the final adsorbed amount of BSA were much less than those of FGN. For the same protein FGN, the adsorption speed and the final amount of adsorbed protein at protein concentration of 30μg/ml were obviously higher than those at concentration of 7.5μg/ml. The main problem for the ellipsometric study of protein adsorption at surfaces of polymeric materials is how to get surface smoothness and reflectivity high enough for the ellipsometric measurement. In this work, a method of polymer film spreading on surface of polished silicon chips has been developed. Samples prepared by this method accorded well with requirement of the ellipsometric measurement. Using ellipsometry, the adsorption behavior of FGN onto the polyurethane surface was preliminarily studied and compared with that on hydrophilic silicon surface. It is shown that the speed of FGN adsorption onto the polyurethane film and the final amount of the adsorbed protein are much less than those onto the hydrophilic silicon surface. It suggests that the hemocompatibility of hydrophilic silicon is much lower than that of polyurethane film. | Adsorption behavior of bovine serum albumin (BSA) and human fibrinogen (FGN) was studied by using ellipsometry. It is shown that the final amount of adsorbed BSA is less than that of FGN at equal protein concentration when the concentration is above 5 μg/ml. With changed protein concentration, the adsorption of BSA is saturated at concentration of 10 μg/ml while the concentration for FGN adsorption saturation is 20 μg/ml. At equal protein concentration of 30 μg/ml, both the adsorption speed and the final adsorbed amount of BSA are much less than those of FGN. For the same protein FGN, the adsorption speed and the final amount of adsorbed protein at protein concentration of 30 μg/ml are obviously higher than those at concentration of 7.5 μg/ml. A method of polymer film spreading on surface of polished silicon chips has been developed. Samples prepared in this method accord with requirement of the ellipsometric measurement. By using ellipsometry, the adsorption behavior of FGN onto the polyurethane surface was preliminarily studied and compared with that on hydrophilic silicon surface. It is shown that the speed of FGN adsorption onto the polyurethane film and the final amount of the adsorbed protein are much less than those onto the hydrophilic silicon surface. It suggests that the hemocompatibility of hydrophilic silicon is much lower than that of polyurethane film.