Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Synthesis Of Bis(4 '-Hydroxyphenyl)-Toluene-2,4-Diurethane For Main Chain Liquid Crystalline Poly(Urethane-Ester)S

Synthesis of bis(4′-hydroxyphenyl)-tolylene-2,4-diurea for main chain thermotropic liquid crystalline poly(urea-ester)s

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Synthesis and characterization of a novel kind of thermotropic liquid crystalline poly(urea-ester)s based on bis(4?-hydroxyphenyl)-tolyene-2,4-diurea

Synthesis and characterization of thermotropic liquid-crystalline polyurethanes containing biphenyl group

Catalytic Mechanisms of Triphenyl Bismuth, Dibutyltin Dilaurate, and Their Combination in Polyurethane-Forming Reaction

Synthesis and Curing of a Novel Combined Liquid Crystalline Epoxy

Synthesis and Liquid Crystalline Properties of New Thermotropic Polyurethanes

Synthesis and Properties of Liquid Crystalline Polyurethanes from 4,4-Bis (6-Hydroxyhexoxy) Biphenyl and 3,3'-Dimethyl-4, 4’-Biphenylene Diisocyanate

Synthesis and Properties of Main-Chain Liquid Crystal Polyurethanes

Synthesis and liquid crystalline behavior of three-arm urethane derivatives bearing protruded alkyoxylbiphenyls

Synthesis and properties of new polyurethanes with triazene moieties in the main chain

Synthesis and Characterization of Thermotropic Liquid Crystal Polyureas Containing Biphenyl Group

Synthesis and Characterization of Novel Highly Branched Block Copoly(urethane‐imide)s Based on Pentaerythritol, Different Diisocyanate and Aromatic Dianhydride

Synthesis and Properties of Main-Chain Liquid Crystalline Polyurethane Elastomers with Azoxybenzene

Synthesis and Properties of Polyurethaneureas with Two Soft Segments of HTPB-PTMG

Sulfonated poly (Ester-Urethane) / ionic liquids systems: synthesis, characterization and properties

One-Shot Synthesis of Thermoplastic Polyurethane Based on Bio-Polyol (Polytrimethylene Ether Glycol) and Characterization of Micro-Phase Separation

A Non-Isocyanate Route to Poly(Ether Urethane): Synthesis and Effect of Chemical Structures of Hard Segment

Synthesis And Thermotropic Liquid-Crystalline Behavior Of Novel Main-Chain Poly(Aryl Ether Ketones)

The Synthesis and Characterization of the Novel Poly(aryl ether ketone)s with Liquid Crystallinity