Electrical properties of 0.94Bi 0.5 Na 0.5 TiO 3 –0.06Ba(Zr 0.055 Ti 0.945 )O 3 lead-free ceramics with high thermal stability
Jun-Jun Wang,Fei-Fei Guo,Bin Yang,Shan-Tao Zhang,Li-Mei Zheng,Feng-Min Wu,Wen-Wu Cao
DOI: https://doi.org/10.1007/s10854-017-8154-1
2017-01-01
Abstract:Here we report the 0.94(Bi 0.5 Na 0.5 )TiO 3 –0.06Ba(Zr 0.055 Ti 0.945 )O 3 (0.94BNT–0.06BZT) lead-free ceramics was synthesized by two-step solid state reaction route. The structural, dielectric, ferroelectric, piezoelectric and electromechanical properties of the ceramics were studied, and showed excellent electric properties ( P s = 39.9 μC/cm 2 , P r = 33.7 μC/cm 2 , E c = 2.79 kV/mm, S = 0.20%, d 33 = 174 pC/N, k p = 0.33). The depolarization temperature ( T d ) of the ceramics is about 65 °C, which is determined from the first hump of relative dielectric constant. The electromechanical factor k p disappears at 65 °C, is consistent with the depolarization temperature ( T d ) and the ferroelectric-antiferroelectric phase transition temperature ( T fe − afe ) determined from the temperature-dependent P – E and bipolar S – E curves. These results indicate the 0.94BNT–0.06BZT ceramics has a good thermal stability in range of − 60–60 °C, and meets the actual demand.