Abstract:Using N,N′-dimethylaminoethyl methacrylate (DMAEMA) as functional co-monomer and styrene (St) as main monomer, the amino-containing hollow latexes were fabricated via one-step emulsion copolymerization and following stepwise acid-alkali post-treatment. Influences of DMAEMA content and post-treatment condition on the morphology and volume expansion of the P(St-co-DMAEMA) latex particles were investigated based on the TEM characterization, and the hollow-forming mechanism was proposed. Results showed that the introduction of 2-butonane promoted the mobility of the polymer chains and the hollow structure generated under moderate post-treatment conditions. Many factors should be balanced to obtain fine hollow particles, an appropriate content of DMAEMA was 15 mol% to all the monomers, and the optimized post-treatment conditions were at 70 °C for 1 h both for acid treatment (initial pH 4.0) and for alkali treatment (initial pH 9.0). Under the optimized conditions, the mean diameter and volume expansion of the resulted hollow particles were 264 nm and 934%, respectively. Finally, the hollow P(St-co-DMAEMA)/laponite composite latex particles were fabricated simply by electrostatic adsorption process, and the resulted composite hollow particles loaded 4.1 wt% of laponite platelets and showed better thermal stability. This simple and facile method can be applied to fabricate the functional hollow latex particles with amino groups including polymeric and polymeric-inorganic composite materials.

Preparation of Porous Latex Particles by Emulsion Polymerization

Stability of the emulsion copolymerization process of the latex containing glycidyl and amino groups

Preparation and Structure Control of Hollow Polymer Particles——Synthesis and Effect on the Hollow Structure of the Core Latex

PREPARATION OF MULTIHOLLOW PARTICLES BY SEEDED EMULSION COPOLYMERIZASION

Preparation and Structure Control of Hollow Polymer Particles: Influence of Seeded Emulsion Polymerization and Alkalization Treatment Process

Synthesis and Characterization of Hollow Polymer Latex Particles

PREPARATION OF HOLLOW LATEX PARTICLES-ALKALI TREATMENT

Preparation of Bicontinuous Porous Polymeric Materials Via Microemulsion Polymerization

Preparation and Structure Control of Hollow Polymer Particles Synthesis a

Influence of Unsaturated Acid Monomer on the Morphology of Latex Particles in the Preparation of Hollow Latex Via the Alkali Post‐treatment

Preparation of Mma-Ba-Dmaema Nanosized Latex

Preparation of Multihollow P(St–MAA) Particles by Sequence Soap-Free/soap Emulsion Polymerization and Followed by Stepwise Alkali/acid Posttreatment

Fabrication of amino-containing hollow polymer latex and its composite with inorganic nanoparticles

Preparation of Porous Pmma Resin by A New Emulsion Polymerization Process and the Mechanism of Particle Formation

Effect of Monomer Feeding Mode on the Preparation of Hollow Latexes with High Maa Content in the Core Latex Preparation

Influences Of The Polymerization Ingredients On The Porous Morphology Of Soap-Free Poly(Methyl Methacrylate/Ethyl Acrylate/Methacrylic Adid) Seeded Latex Particles

Morphological evolution of multistage polymer particles in the alkali post-treatment

Preparation of Hollow Polymer Microspheres——Effect of Acid Monomer Content

Morphology Control of Soap-Free Seeded P(St–EA–AA) Latex Particles

Preparation of Bowl‐Like Polymer Particles Via Multi‐Step Emulsion Polymerization and Alkali Post‐Treatment

Influences of the Polymerization Ingredients on the Porous Morphology of Soap‐free Poly(methyl Methacrylate/ethyl Acrylate/methacrylic Acid) Seeded Latex Particles