Relationship among thermal anomalies, superconductivity and structural blocks in different-metal-site-doped YBCO
L Zhang,X F Sun,Y Z Wang,H L Du,H Zhang
DOI: https://doi.org/10.1088/0953-8984/20/7/075209
2008-01-01
Abstract:Three series of polycrystalline samples of YBa(2)Cu(3- x)Ni(x)O(y)(YBCNO), Y(1-x)Pr(x)Ba(2)Cu(3)O(y) (YPrBCO) and YBa(2-x)La(x)Cu(3)O(y) (YBLCO) (x = 0, 0.05, 0.10, 0.15, 0.20, 0.25, respectively), synthesized by a solid state reaction technique, were characterized by thermogravimetry, differential scanning calorimetry, DC magnetization measurement, temperature dependent x-ray diffraction and Rietveld refinement. To our knowledge this is the first systematic report of two phase transitions at about 400 and 850 degrees C before melting. By careful measurements it was seen that the amounts of the percentage weight loss and the DSC changes, along with T(c), decrease with increasing dopant. Combining the theory of oxygen diffusion with the block model in YBCO, the mechanism of the phase transitions can be explained as follows: the phase transition at 400 degrees C comes directly from O(1) in the rock salt block, while the phase transition at 850 degrees C is related to the perovskite block. The calculation of the combinative energy between the two structural rock salt and perovskite blocks shows that, with increasing dopant, the higher the combinative energy the lower the T(c), and vice versa. The results indicate that there exits a triangular relationship among thermal anomalies, superconductivity and structural blocks in different-metal-site-doped YBCO, which may be significant for understanding the mechanism of high-temperature superconductivity.