Unknown Phase Transitions, Superconductivity and Structural Blocks in YBa2Cu3−xNixO7−δ
L. Zhang,Y. Z. Wang,Y. Jcui,H. L. Du,H. Zhang
DOI: https://doi.org/10.1088/0953-2048/21/02/025008
2008-01-01
Superconductor Science and Technology
Abstract:Polycrystalline samples of YBa(2)Cu(3-x)Ni(x)O(7-delta) (x = 0, 0.05, 0.10, 0.15, 0.20, and 0.25) (YBCNO) were investigated by means of differential scanning calorimetry, thermogravimetry, temperature dependent x-ray diffraction, Rietveld refinement with the help of the bond valence sum method, magnetic moment-temperature measurement and combinative energy calculation between the two structural blocks, perovskite and rock salt. It was observed that there are two thermal anomalies of weight loss and heat flow change at about 400 and 850 degrees C in each sample before melting. By careful measurement it was found that the weight loss and endothermal absorption, as well as the critical temperature T(c), decrease with the increase of dopant. Combining the theory of oxygen diffusion with the block model in YBCO, the mechanism of the phase transitions can be explained as follows: the phase transition at 400 degrees C comes directly from O(1) in the rock salt block, while the phase transition at 850 degrees C corresponds to O(2) and O(3) in the Cu(2)-O plane. When a phase transition occurs, the oxygen at O(2) and O(3) sites is rearranged and a few oxygen atoms enter the O(1) site of the Cu(1)-O plane through the O(4) bridge atoms, finally escaping from the crystal cell. Thus the phase transition at 850 degrees C is related to the perovskite block. The calculation of the combinative energy between the rock salt and perovskite blocks shows that with increasing Ni content, the higher the combinative energy and the lower the T(c). The results indicate that there is a close relationship among thermal phase transitions, superconductivity and structural blocks in YBCNO, which may be significant for understanding the mechanism of high temperature superconductivity.