Abstract:Four catalysts were prepared in our previous work using the solution combustion method, incipient-wetness impregnation method, colloid mill circulating impregnation method, and hydrothermal-precipitation method, respectively, labeled as SCM, IMP, T310, and HTP. And the performance (stability) of the four catalysts for CO2 reforming of CH4 was investigated at 800 °C. In this paper, the composition and structure characteristics of the deposited carbon on the above four catalysts were tested through TEM, Raman, TPH, and TG-DTG technologies. The results showed that filamentous carbon was the primary type of carbon deposition on the catalysts, and a large amount of accumulated carbon would block the catalyst pores, affecting the catalytic performance. The carbon deposited on the catalyst prepared using the hydrothermal-precipitation method calcined at 800 °C exhibited a high degree of graphitization, and the proportion of graphitized carbon was considerable, which is harmful to the stability of the catalyst. The decarburization temperature of the deposited carbon on the four catalysts was mainly in the range of 500–700 °C. Using the Coats–Redfern model, as the reaction order was set as 1, 2, 3, 4, and 5, the decarburization activation energy ranged between 50 and 80 kJ/mol.

Preparation and characterization of catalysts used in CH4/CO2 reforming reaction

Catalytic Performance and Characterization of Ni–CaO–ZrO2 Catalysts for Dry Reforming of Methane

Preparation of Ni-Co/SiO2 catalyst by ammonia reflux impregnation and its CH4-CO2 reforming reaction performance

Performance of supported nickel catalyst for reforming of CH 4 with CO 2 to syngas: I. Effect of preparation conditions and Ni loading

Effects of Supports on the Activity of Nickel Catalyst for Ch4 Reforming with Co2

Effects of Promoters and Preparation Procedures on Reforming of Methane with Carbon Dioxide over Ni/Al2O3 Catalyst

Performance of supported nickel catalyst for reforming of CH 4 with CO 2 to syngas: II . Effect of basic promoters

Supported Cobalt Catalyst Promoted by Noble Metals for CH4/CO2 Reforming to SyngasⅠ.Preparation Conditions and Performance of Pt-Co/Al2O3 Catalyst

Progress in Ni-based catalysts for CH4-CO2 reforming reaction

Structure Characteristics and Removal Behavior of the Deposited Carbon on Ni-Al2O3 Catalyst for CO2 Reforming of CH4

Studies on carbon deposition of Ni catalyst in CH4-CO2 reforming reaction

Carbon Dioxide Reforming of Methane over Ni-based Catalyst

Combined steam and CO2 reforming of methane over Co–Ce/AC-N catalyst: Effect of preparation methods on catalyst activity and stability

Promotional Effect of Ni−Sn Interaction over Ni Supported on Sn‐incorporated MCM‐41 Catalysts for CO 2 Reforming of CH 4

Characterization of Ca-promoted Ni/α-Al2O3 Catalyst for CH4 Reforming with CO2

Enhancement of the catalytic performance and coke resistance of alcohol-promoted Ni/MCM-41 catalysts for CH4/CO2 reforming

Sensitivity of the properties and performance of Co catalyst to the nature of support for CO2 reforming of CH4

Research on nickel-based catalyst in carbon dioxide reforming of methane

Studies on Catalysts of Anti-Carbon Deposition for Ch4 Reforming with Co2

Carbon Dioxide Reforming of Methane over Cobalt‐Nickel Bimetal‐Doped Ordered Mesoporous Alumina Catalysts with Advanced Catalytic Performances

Catalytic performance of CH4–CO2 reforming over metal free nitrogen-doped biomass carbon catalysts: Effect of different preparation methods